RAPIDLY SOLIDIFIED Al-Fe ALLOY FLAKES BY ATOMIZATION-ROLLING PROCESS.

被引：0
|
作者：
Shibue, Kazuhisa [1 ]
Sano, Hideo [1 ]
Yamauchi, Shigenori [1 ]
Inumaru, Susumu [1 ]
机构：
[1] Sumitomo Light Metal Industries Ltd, Jpn, Sumitomo Light Metal Industries Ltd, Jpn
来源：
Sumitomo Keikinzoku Giho/Sumitomo Light Metal Technical Reports | 1987年 / 28卷 / 04期
关键词：
ALUMINUM METALLOGRAPHY - Microstructure - POWDER METAL PRODUCTS - Mechanical Properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Al-2,4,6,8 and 10%Fe alloys were rapidly solidified by means of atomization-rolling which is a combined process of gas atomization using a single roller. Microstructure of the flake was finer than that of atomized powder. From the cell spacing of the flake, the cooling rate is estimated at 10**5-10**7 degree C/sec. The lattice constant decreased with Fe content and reached a constant value beyond 4% Fe content. The solubility of Fe was estimated at 1. 4% in the flake containing more than 4%. Hardness increased with Fe content. It was higher than that of gas atomized powder.
引用
收藏
页码：181 / 186
相关论文
共 50 条
  • [41] MICROSTRUCTURE AND AGING OF A RAPIDLY SOLIDIFIED FE-AL-B ALLOY
    SEVERN, ET
    VEDULA, K
    JOURNAL OF METALS, 1983, 35 (08): : A53 - A53
  • [42] Structure of Rapidly Solidified Al-Fe-Cr-Ce Alloy
    Michalcova, Alena
    Vojtech, Dalibor
    Novak, Pavel
    Prochazka, Ivan
    Cizek, Jakub
    Drahokoupil, Jan
    Wienerova, Katerina
    Saksl, Karel
    Rokicki, Pawel
    Spotz, Zdenek
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE, 2011, 465 : 199 - +
  • [43] THE STRUCTURE OF A RAPIDLY SOLIDIFIED AL-FE-TI-C ALLOY
    TONG, XC
    SHEN, NF
    LIU, BC
    JOURNAL OF MATERIALS SCIENCE, 1995, 30 (14) : 3680 - 3689
  • [44] MICROSTRUCTURE OF RAPIDLY SOLIDIFIED FE-C-CR ALLOY PARTICLE BY CENTRIFUGAL ATOMIZATION METHOD
    OGAWA, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (12): : S971 - S971
  • [45] PRODUCTION OF RAPIDLY SOLIDIFIED FE-C-SI ALLOY POWDER BY THE ROTATING-WATER-ATOMIZATION PROCESS AND ITS STRUCTURE
    YAMAUCHI, I
    NOMURA, Y
    OHNAKA, I
    MATSUMOTO, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (09): : 1138 - 1145
  • [46] PRODUCTION AND STRUCTURE OF RAPIDLY SOLIDIFIED FE-C-SI ALLOY POWDER PRODUCED BY ROTATING-WATER-ATOMIZATION PROCESS
    YAMAUCHI, I
    OHNAKA, I
    NOMURA, Y
    MATSUMOTO, Y
    FUKUSAKO, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 26 (04) : B137 - B138
  • [47] PRODUCTION AND PROPERTIES OF RAPIDLY SOLIDIFIED AL-4.5-PERCENT CU ALLOY POWDER BY THE ROTATING-WATER-ATOMIZATION PROCESS
    OHNAKA, I
    YAMAUCHI, I
    KAWAMOTO, S
    FUKUSAKO, T
    JOURNAL OF MATERIALS SCIENCE, 1985, 20 (06) : 2148 - 2158
  • [48] Morphology and distribution of Al3Fe phase in hypereutectic Al-Fe alloy solidified under magnetic field
    Ban Chunyan
    ChinaFoundry, 2011, 8 (04) : 386 - 391
  • [49] Morphology and distribution of Al3Fe phase in hypereutectic Al-Fe alloy solidified under magnetic field
    Ban Chunyan
    Zhang Jianfeng
    Qian Peng
    Zhang Xu
    Han Yi
    Cui Jianzhong
    CHINA FOUNDRY, 2011, 8 (04) : 386 - 391
  • [50] DIFFUSION OF FE IN A DILUTE AL-FE ALLOY
    ELSAYED, H
    KOVACS, I
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 1974, 24 (01): : K45 - K47
12345