RELATION OF PROCESSING VARIABLES IN THERMOMECHANICAL TREATMENT TO STRENGTH, DUCTILITY, AND TOUGHNESS OF 280 kg/mm2 GRADE MARAGING STEEL.

被引：0
作者：
Kawabe, Yoshikuni
Muneki, Seiichi
Nakazawa, Kozo
机构：
来源：
Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan | 1978年 / 64卷 / 07期
关键词：
D O I：
10.2355/tetsutohagane1955.64.7_1063
中图分类号：
学科分类号：
摘要：
The mechanical properties of 13Ni-15Co-10Mo steel have been investigated. The austenite grain size attainable is greatly affected by the reduction in rolling. The grain refinement increases the tensile strength and ductility, but does not improve fracture toughness. The anisotropies of strength and ductility are related to the unrecrystallized austenite grain, whereas the anisotropy of fracture toughness is not observed for all conditions.
引用
收藏
页码：1063 / 1071
相关论文
共 50 条
[31]   IMPROVEMENT IN TOUGHNESS OF LARGE HEAT-INPUT WELD BOND OF 60 kg/mm2 GRADE HIGH TENSILE STRENGTH STEEL PLATES DUE TO BORON ADDITION AND LOW SILICON CONTENT. [J].
Ohtani, Hiroo ;
Watanabe, Seiichi ;
Kawaguchi, Yoshiaki ;
Yamaguchi, Yoji .
1978, 64 (14) :2205-2214
[32]   PROPERTIES OF 60kg/mm2 HIGH TENSILE STRENGTH STEEL PLATE WITH EXTREMELY THICKNESS. [J].
Izeki, Yoshihiro ;
Maruyama, Kaichiro ;
Watanabe, Yuichi .
Sumitomo Metals, 1973, 25 (04) :121-131
[33]   ADVANCED HIGH TENSILE STRENGTH STEEL OF 100 kgf/mm2 GRADE FOR PENSTOCK USE. [J].
Shimoda, Ryuji ;
Matsuura, Toshihiko ;
Kure, Yoshihiro ;
Watanabe, Itaru ;
Suzuki, Motoaki ;
Sakui, Shin .
Transactions of the Japan Welding Society, 1987, 18 (02) :77-85
[34]   TENSILE-STRENGTH OF 80 KGF/MM2 GRADE STEEL FOR HIGH HEAT INPUT WELDING [J].
SUGA, M ;
SAKUI, S ;
TAKAHASHI, K ;
WATANABE, I .
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (05) :B155-B155
[35]   DEVELOPMENT OF HOT-ROLLED HIGH STRENGTH STEEL SHEETS FOR FORMABILITY WITH 50 AND 60 kg/mm2 IN TENSILE STRENGTH. [J].
Kawakami, Koichi ;
Hase, Noboru ;
Sugisawa, Seichi ;
Toyota, Yuji ;
Arai, Tetsuzo .
Sumitomo Metals, 1974, 26 (02) :10-17
[36]   NEW PROCESS FOR PRODUCING 80 KG/MM2 GRADE HEXAGONAL BOLTS FROM THE HIGH-STRENGTH WIRE ROD [J].
OCHIAI, I ;
SERIKAWA, O ;
YOSHIMURA, T ;
OHGA, T ;
TODA, M .
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (07) :B252-B252
[37]   DEVELOPMENT OF TENSILE STRENGTH 50 kgf/mm2 GRADE STEEL PLATES FOR ARCTIC OFFSHORE STRUCTURES WITH HIGH TOUGHNESS IN LARGE HEAT INPUT WELDS (INVESTIGATION OF LARGE HEAT INPUT WELDABILITY OF STEEL PLATES WITH 50 kgf/mm2 GRADE FOR ARCTIC OFFSHORE STRUCTURES III). [J].
Furusawa, Jun ;
Arimochi, Kazushige ;
Watanabe, Seiichi ;
Kurayasu, Hirofumi ;
Bessyo, Kiyoshi ;
Nakano, Naokazu ;
Suzuki, Shu-ichi .
Transactions of the Iron and Steel Institute of Japan, 1986, 27 (01)
[38]   IMPROVEMENT OF FRACTURE-TOUGHNESS OF WELDED REGION FOR HIGH-STRENGTH 90 KGF/MM2 STEEL CHAIN [J].
SAKAMOTO, M .
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (05) :S655-S655
[39]   TENSILE-STRENGTH OF 80-KGF/MM2 GRADE STEEL FOR HIGH HEAT INPUT WELDING [J].
SUGA, M .
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (13) :1385-1385
[40]   ON BEHAVIOR OF PRECIPITATES IN NB-MO HEAT-TREATED HIGH STRENGTH STEEL HAVING 80 KG/MM2 TENSILE STRENGTH [J].
KANAZAWA, S ;
NAKASHIMA, A ;
OKAMOTO, K ;
TANABE, K ;
NAKAZAWA, S .
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1967, 8 (02) :113-+
12345