HOT ROLLED STEEL SHEET WITH EXCELLENT DEEP DRAWABILITY, 'KFN3'.

被引：0

作者：

Sakata, Kei ^{[1
]}

Hashiguchi, Koichi ^{[1
]}

Okano, Shinobu ^{[1
]}

Higashino, Tateo ^{[1
]}

Inoue, Masataka ^{[1
]}

Sato, Susumu ^{[1
]}

机构：

[1] I & S Research Lab, Jpn, I & S Research Lab, Jpn

来源：

Kawasaki Steel Technical Report | 1988年 / 18期

关键词：

METAL DRAWING - Deep - ROLLING MILL PRACTICE - Hot Rolling - SHEET AND STRIP METAL - Forming - STEEL - Drawing;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Hot rolled steel sheet with extra-low carbon content which exhibits excellent formability has been newly developed in Kawasaki Steel. Chemical composition of this steel is specially controlled, that is to say, sulfur content is 0. 003 wt percent or less and titanium is added so that the effective Ti/C atomic ratio will come to more than 1. 0. In the hot rolling process, this steel is coiled at a temperature lower than 600 degree C. The characteristics of this steel are as follows: 1) total elongation is 55 percent or higher (3. 2 mm thick); 2) planar anisotropy is minimal in spite of Ti-addition; 3) this steel exhibits a higher resistance to cold-work brittleness due to the control of both residual solute carbon content and fine grain sizes.

引用

页码：52 / 60