The fracture toughness of Mg2Si determined by 3-point bending and the indentation microcracking method

被引：0

作者：

Milekhine, V. ^{[1
]}

Solberg, J.K. ^{[1
]}

Onsøien, M.I. ^{[2
]}

机构：

[1] Norwegian University of Science and Technology, Trondheim

[2] Sintef Materials Technology, Trondheim

来源：

International Journal of Materials Research | 2022年 / 94卷 / 12期

关键词：

Fracture toughness; Indentation microcracking; Intermetallics; Mg[!sub]2[!/sub]Si;

D O I：

10.1515/ijmr-2003-0240

中图分类号：

学科分类号：

摘要：

The Mg2Si intermetallic compound was produced from the raw materials by melting in a vacuum furnace. The purity of the as-cast material was 98 vol.%. Continuous polishing of a surface containing microhardness indentation marks showed that the cracks initiated by the indenter were of the Palmqvist type. Equations developed by Niihara and Shetty et al. were applied on the data extracted from the microhardness indentations for calculating the fracture toughness of Mg2Si, and the average KIC values were found to be 0.80 and 0.62 MPa · m1/2, respectively. The KIC value found from Shetty's equation is close to the experimental value of 0.64 MPa · m1/2 found by a three-point bending test. © 2022 Carl Hanser Verlag. All rights reserved.