Pore formation during reactive sintering of extruded titanium-aluminum powder mixtures

被引：0

作者：

Dahms, M. ^{[1
]}

Leitner, G. ^{[1
]}

Poessnecker, W. ^{[1
]}

Schultrich, S. ^{[1
]}

Schmelzer, F. ^{[1
]}

机构：

[1] Fraunhofer-Einrichtung fuer, Keramische Technologien und, Sinterwerkstoffe, Dresden, Germany

来源：

Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques | 1993年 / 84卷 / 05期

关键词：

Aluminum alloys - Calorimetry - Diffusion in solids - Dilatometers - Metal extrusion - Microstructure - Mixtures - Phase transitions - Porosity - Sintering - Swelling - Titanium alloys;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

A powder mixture Ti-49 at.% Al was extruded at room temperature. Swelling due to phase transformation during annealing was studied using differential scanning calorimetry and dilatometry. It is the result of several processes: (i) Kirkendall pores during solid state interdiffusion, (ii) macro-pores during the reaction of liquid aluminum and solid titanium, (iii) interdiffusion of Al3Ti and pure titanium forming the intermetallic phases γ-TiAl and α2-Ti3Al. Swelling is anisotropic due to the elongated titanium particles. Sintering occurs at higher temperatures depending on the microstructure after Al3Ti formation. For technological applications, minimization of porosity is possible by optimization of the time-temperature path.

引用

页码：351 / 357

共 50 条

[41] Pore collapse in powder metal mixtures during shock compression
Reding, D. J.
JOURNAL OF APPLIED PHYSICS, 2009, 105 (08)
[42] Features of In Situ Structure Formation in Powder Materials Based on Titanium and Refractory Compound during Vacuum Sintering
Korosteleva, E. N.
Pribytkov, G. A.
Korzhova, V. V.
Krinitcyn, M. G.
PROCEEDINGS OF THE ADVANCED MATERIALS WITH HIERARCHICAL STRUCTURE FOR NEW TECHNOLOGIES AND RELIABLE STRUCTURES, 2018, 2051
[43] Reactive Sintering Mechanism and Phase Formation in Ni-Ti-Al Powder Mixture During Heating
Salvetr, Pavel
Skolakova, Andrea
Hudrisier, Cyprien
Novak, Pavel
Vojtech, Dalibor
MATERIALS, 2018, 11 (05)
[44] Formation of TiCX during reactive spark plasma sintering of mechanically milled Ti/carbon nanotube mixtures
Vasanthakumar, K.
Karthiselva, N. S.
Chawake, Niraj M.
Bakshi, Srinivasa Rao
JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 709 : 829 - 841
[45] Hot deformation behavior and microstructural evolution of titanium-aluminum based alloy during hot compression
Duan, Z. X.
Chen, H.
Shen, Y. X.
Liu, L. P.
Feng, X. R.
Song, X. L.
Zou, H. H.
Han, Y.
Ran, X.
Chens, H.
MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2024, 55 (10) : 1395 - 1405
[46] Different Formation Routes of Pore Structure in Aluminum Powder Metallurgy Alloy
Bidulska, Jana
Bidulsky, Robert
Grande, Marco Actis
Kvackaj, Tibor
MATERIALS, 2019, 12 (22)
[47] Bulk changes and structurization in solid-phase sintering of titanium–silicon powder mixtures
E. N. Korosteleva
G. A. Pribytkov
A. V. Gurskikh
Powder Metallurgy and Metal Ceramics, 2009, 48 : 8 - 12
[48] PROCESSING OF IRON-TITANIUM POWDER MIXTURES BY TRANSIENT LIQUID-PHASE SINTERING
GERMAN, RM
DUNLAP, JW
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (02): : 205 - 213
[49] Reactive synthesis and characterization of titanium aluminides produced from elemental powder mixtures
H. Sina
S. Iyengar
Journal of Thermal Analysis and Calorimetry, 2015, 122 : 689 - 698
[50] Porous Titanium Parts Fabricated by Sintering of TiH2 and Ti Powder Mixtures
Qin Peng
Bin Yang
Bernd Friedrich
Journal of Materials Engineering and Performance, 2018, 27 : 228 - 242

← 1 2 3 4 5 →