Effect of Welding Defects at the Fusion Boundary on Static Strength of the Weld Joint in Large-Diameter Pipes.

被引：0
|
作者：
Shakhmatov, M.V.
Erofeev, V.V.
Lupin, V.A.
Ostsemin, A.A.
机构：
来源：
Problemy Prochnosti | 1984年 / 08期
关键词：
NATURAL GAS PIPELINES - PETROLEUM PIPELINES - PIPE - Welding - PIPELINES - Welding;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A calculations procedure based on the slip-line method is suggested for estimating the stressed state and static strength of weld joints with nonthrough defects at the fusion boundary of a hard weld and soft basic metal is suggested. The analytical solution of the problem takes into account the defect place, stressed state volume in the concave cross-section and mechanical properties of the weld joint. This underlies determination of admissible defect sizes which do not reduce the weld joint strength in pipes of large diameter. Experimental check showed a satisfactory agreement between the results.
引用
收藏
相关论文
共 50 条
  • [31] Buckling Strength of Profiled Large-Diameter Rigid PVC Pipes Exposed to Outside Pressure.
    Barth, E.
    Schommer, R.
    Kunststoffe, 1975, 65 (02): : 85 - 88
  • [32] TECHNOLOGY FOR WELDING LARGE-DIAMETER BRANCH PIPES TO DRUMS OF HIGH-PRESSURE STEAM-GENERATORS
    PARSHIN, AA
    AUTOMATIC WELDING USSR, 1976, 29 (09): : 30 - 33
  • [33] Comparative study on the performance of butt fusion-welding processes for nuclear safety class large-diameter thick-walled PE pipes
    Wang, Zhenchao
    Wang, Bin
    Xiang, Aimin
    Jiao, Di
    Yu, Fa
    Zhang, Qiuju
    Zhao, Xiaoying
    NUCLEAR ENGINEERING AND TECHNOLOGY, 2024, 56 (10) : 4184 - 4194
  • [34] Evaluation of the crack resistance and mechanical properties of the metal of large-diameter pipes under static and dynamic loads
    Ostsemin A.A.
    Saidov G.I.
    Strength of Materials, 2004, 36 (04) : 391 - 401
  • [35] Evaluation of the crack resistance and mechanical properties of the metal of large-diameter pipes under static and dynamic loads
    Ostsemin, A.A.
    Saidov, G.I.
    Problemy Prochnosti, 2004, (04): : 80 - 93
  • [36] Effect of annealing atmospheres on the void defects in large-diameter CZSi single crystals
    Liu, Caichi
    Hao, Qiuyan
    Zhang, Jianqiang
    Sun, Shilong
    Teng, Xiaoyun
    Zhao, Yanqiao
    Sun, Haizhi
    Zhou, Qigang
    Wang, Jing
    MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING, 2006, 9 (1-3) : 117 - 120
  • [37] Effect of intrinsic point defects on copper precipitation in large-diameter Czochralski silicon
    Xi, ZQ
    Yang, DR
    Xu, J
    Ji, YK
    Que, DL
    Moeller, HJ
    APPLIED PHYSICS LETTERS, 2003, 83 (15) : 3048 - 3050
  • [38] IMPROVING THE FATIGUE-STRENGTH OF WELD METAL IN LARGE DIAMETER MICRO-ALLOYED STEEL PIPES
    MANDELBERG, SL
    BOGACHEK, YL
    KOVALEVSKII, VA
    TOKAREV, VS
    AUTOMATIC WELDING USSR, 1986, 39 (01): : 38 - 41
  • [39] Static strength of welded joint with the hard interlayers and defects along the fusion line
    Dilman, V.L.
    Ostsemin, A.A.
    Svarochnoe Proizvodstvo, 2004, (05): : 3 - 7
  • [40] Effect of stress concentration in a welded seam on the low-cycle fatigue of large-diameter pipes
    Ostsemin, AA
    Dil'man, VL
    CHEMICAL AND PETROLEUM ENGINEERING, 2003, 39 (5-6) : 259 - 264
12345