EFFECT OF SMALL DEFECTS ON THE FATIGUE PROPERTIES OF MEDIUMSTRENGTH CAST STEEL

被引：0

作者：

DE KAZINCKY F

机构：

来源：

| 1970年 / 208卷 / pt 9期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Small defects, such as microshrinkage cavities or pores, act as stress raisers and may initiate fatigue fracture. The effect of defect size on the gatigue strength was investigated in cast steels of 800, 880, and 1040 MN/sq m tensile strength, respectively. This was compared with corresponding results for mild steels, evaluated from earlier investigations. It was shown that fatigue-strength reduction increases with increasing tensile strength. Microshrinkage cavities at the specimen surface caused a larger strength reduction thanhose located in the interior. Pores were found to have a more severe effect than microshrinkage cavities of the same size.

引用

页码：851 / 855

共 50 条

[41] Inclined defects and their effect on the fatigue limit and small crack growth [J].

Roiko, Andrew ;

Solin, Jussi ;

Murakami, Yukitaka .

FDMD II - JIP 2014 - FATIGUE DESIGN & MATERIAL DEFECTS, 2014, 12

[42] Effect of small defects on the fatigue strength of martensitic stainless steels [J].

Schoenbauer, Bernd M. ;

Mayer, Herwig .

INTERNATIONAL JOURNAL OF FATIGUE, 2019, 127 :362-375

[43] Effect of Surface Finishing State on Fatigue Strength of Cast Aluminium and Steel Alloys [J].

Oberreiter, Matthias ;

Horvath, Michael ;

Stoschka, Michael ;

Fladischer, Stefan .

MATERIALS, 2023, 16 (13)

[44] Effect of Thermal Aging on Environmental Fatigue Life of Cast Austenitic Stainless Steel [J].

Wang, Yimei ;

Xiao, Qingshan ;

Chen, Yinqiang ;

Liu, Tingguang .

Yuanzineng Kexue Jishu/Atomic Energy Science and Technology, 2024, 58 (08) :1628-1634

[45] Defects in Continuously Cast Steel - 1. [J].

Baumann, Hans G. ;

Loepmann, Werner J . .

Drahtwelt, 1973, 59 (11) :469-476

[46] Low Cycle Fatigue of Cast Austenitic Steel [J].

Wu, Xijia ;

Quan, Guangchun ;

Sloss, Clayton .

FATIGUE AND FRACTURE TEST PLANNING, TEST DATA ACQUISITIONS AND ANALYSIS, 2017, 1598 :37-57

[47] THE FATIGUE-STRENGTH OF FORGED AND CAST STEEL [J].

KUDRAVTSEV, IV .

SOVIET ENGINEERING RESEARCH, 1982, 2 (12) :50-52

[48] Fatigue of 8630 cast steel in the presence of porosity [J].

Sigl, KM ;

Hardin, RA ;

Stephens, RI ;

Beckermann, C .

INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2004, 17 (03) :130-146

[49] Influence of defects on the fatigue life of ductile cast iron with as-cast surfaces [J].

Yamaura, H ;

Sekiguchi, K .

DUCTILE IRON SOCIETY'S 1998 KEITH D MILLIS WORLD SYMPOSIUM ON DUCTILE IRON, 1998, :433-453

[50] Effect of sampling position from cast blocks on fatigue properties for spheroidal graphite cast iron [J].

Fukuyama, Kunio ;

Hasegawa, Norihiko ;

Nishikawa, Yuji .

Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1994, 60 (576) :1734-1739

← 1 2 3 4 5 →