EFFECT OF SMALL DEFECTS ON THE FATIGUE PROPERTIES OF MEDIUMSTRENGTH CAST STEEL

被引：0

作者：

DE KAZINCKY F

机构：

来源：

| 1970年 / 208卷 / pt 9期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Small defects, such as microshrinkage cavities or pores, act as stress raisers and may initiate fatigue fracture. The effect of defect size on the gatigue strength was investigated in cast steels of 800, 880, and 1040 MN/sq m tensile strength, respectively. This was compared with corresponding results for mild steels, evaluated from earlier investigations. It was shown that fatigue-strength reduction increases with increasing tensile strength. Microshrinkage cavities at the specimen surface caused a larger strength reduction thanhose located in the interior. Pores were found to have a more severe effect than microshrinkage cavities of the same size.

引用

收藏

页码：851 / 855

相关论文

共 50 条

[31] EFFECT OF SEGREGATIONS IN STRAND CAST STEEL ON THE MATERIAL PROPERTIES [J].

BERSCH, B ;

DEBOER, H ;

BRAND, WD ;

EHRHARDT, H ;

FLOSSDORF, FJ ;

GEBEL, W ;

GULDEN, H ;

KOHLER, HJ ;

RICHTER, K ;

ROTH, G .

STAHL UND EISEN, 1986, 106 (07) :323-331

[32] Cast steel properties [J].

[33] Scale and Surface Machining Quality Effect on Fatigue Properties for China Railway Grade B Cast Steel Wheel [J].

Zhao, Y. X. ;

Yang, B. ;

Li, Y. .

MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 :363-+

[34] Effect of Welding Defects on Fatigue Properties of SWA490BW Steel Cruciform Welded Joints [J].

Xu, Xingyuan ;

Xie, Liyang ;

Zhou, Song ;

An, Jinlan ;

Huang, Yanqing ;

Liu, Youcheng ;

Jin, Lei .

MATERIALS, 2023, 16 (13)

[35] Effects of small defects, matrix structures and loading conditions on the fatigue strength of ductile cast irons [J].

Endo, Masahiro ;

Yanase, Keiji .

THEORETICAL AND APPLIED FRACTURE MECHANICS, 2014, 69 :34-43

[36] INFLUENCE OF SMALL SURFACE DEFECTS ON FATIGUE LIMIT OF NITRIDED AND SHOT PEENING STEEL [J].

Pariente, Fernandez ;

Bagherifard, S. ;

Ghelichi, R. ;

Guagliano, M. .

ADVANCES IN FRACTURE AND DAMAGE MECHANICS VIII, 2010, 417-418 :57-+

[37] Fatigue behavior of nitrided and shot peened steel with artificial small surface defects [J].

Fernandez-Pariente, I. ;

Bagherifard, S. ;

Guagliano, M. ;

Ghelichi, R. .

ENGINEERING FRACTURE MECHANICS, 2013, 103 :2-9

[38] THE INFLUENCE OF MACHINING DEFECTS AND INCLUSIONS ON THE FATIGUE PROPERTIES OF A HARDENED SPRING STEEL [J].

BERGENGREN, Y ;

LARSSON, M ;

MELANDER, A .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1995, 18 (10) :1071-1087

[39] The influence of interacting small defects on the fatigue limits of a pure iron and a bearing steel [J].

Aman, Mari ;

Wada, Kentaro ;

Matsunaga, Hisao ;

Remes, Heikki ;

Marquis, Gary .

INTERNATIONAL JOURNAL OF FATIGUE, 2020, 135

[40] Influence of machining defects and inclusions on the fatigue properties of a hardened spring steel [J].

Bergengren, Y. ;

Larsson, M. ;

Melander, A. .

Fatigue and Fracture of Engineering Materials and Structures, 1995, 18 (10) :1071-1087

← 1 2 3 4 5 →