Influence of mold heat flux on longitudinal surface cracks during high-speed continuous casting of steel slab

被引：0
|
作者：
Nakajima, Keiji [1 ]
Hiraki, Sei [1 ]
Kawamoto, Masayuki [1 ]
Kanazawa, Takashi [1 ]
机构：
[1] Iron and Steel Research Lab
来源：
Sumitomo Search | 1994年 / 55期
关键词：
Addition reactions - Cracks - Defects - Fluxes - Metal castings - Molds - pH - Physical properties - Powder metals - Steel - Temperature measurement - Zirconia;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Influence of mold heat flux on longitudinal cracks were investigated for steel slabs during high casting speed of up to 5m/min with an experimental continuous casting machine. Critical heat flux was found the occurrence of longitudinal cracks on the wide face of slabs were observed in the cast with alminium killed low carbon steel. The reduction of heat flux in mold under the critical value was necessary for the prevention of the defect. It was achieved effectively by the increase of powder basicity and the addition of ZrO2.
引用
收藏
页码：32 / 39
相关论文
共 50 条
  • [1] Investigation of longitudinal surface cracks in a continuous casting slab of high-carbon steel
    GUO Liangliang
    XU Zhengqi
    SHI Jianbin
    HUANG Zongze
    Baosteel Technical Research, 2014, 8 (02) : 19 - 25
  • [2] FACTORS AFFECTING THE FORMATION OF SHELL AND LONGITUDINAL CRACKS IN MOLD DURING HIGH-SPEED CONTINUOUS-CASTING OF SLABS
    NAKATO, H
    OZAWA, M
    KINOSHITA, K
    HABU, Y
    EMI, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 24 (11) : 957 - 965
  • [3] Heat transfer behavior and homogenous solidification control for high-speed continuous casting slab mold
    Zhu M.-Y.
    Cai Z.-Z.
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2022, 44 (04): : 703 - 711
  • [4] Fuzzy estimation for heat flux distribution at the slab continuous casting mold surface
    Chen, Hong
    Su, Litao
    Wang, Guangjun
    Wan, Shibin
    Zhang, Lihui
    Luo, Zhaoming
    INTERNATIONAL JOURNAL OF THERMAL SCIENCES, 2014, 83 : 80 - 88
  • [5] Mold flux developments for high speed slab casting
    Moore, JA
    Camino, C
    Diehl, S
    Phillips, RJ
    Piwinski, D
    79TH STEELMAKING CONFERENCE PROCEEDINGS, 1996, 79 : 259 - 264
  • [6] Heat transfer in mold flux-layers during slab continuous casting
    Chavez, JF
    Celaya, A
    Barron, MA
    Morales, RD
    79TH STEELMAKING CONFERENCE PROCEEDINGS, 1996, 79 : 321 - 329
  • [7] ANALYSIS OF LIQUID FLUX CONSUMPTION MECHANISM FOR SLAB CONTINUOUS CASTING MOLD WITH HIGH CASTING SPEED
    Meng Xiangning
    Zhu Miaoyong
    ACTA METALLURGICA SINICA, 2009, 45 (04) : 485 - 489
  • [8] Mold flux for high speed continuous casting of hypoperitectic steel slabs
    Hanao, A
    Kawamoto, M
    Hara, M
    Murakami, T
    Kikuchi, H
    Hanazaki, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2002, 88 (01): : 23 - 28
  • [9] Mold flux for high speed continuous casting of hypoperitectic steel slabs
    Hanao, M.
    Kawamoto, M.
    Murakami, T.
    Kikuchi, H.
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 2006, 103 (02): : 82 - 88
  • [10] Control of Surface Longitudinal Cracks During the Steel Continuous Casting
    Wang, Fengkang
    Zeng, Jie
    Wang, Wanlin
    TMS 2024 153RD ANNUAL MEETING & EXHIBITION: SUPPLEMENTAL PROCEEDINGS, 2024, : 1031 - 1039
12345