Electrical resistometry of Mg-based microcrystalline alloys and Mg-based composites

被引：0
|
作者：
Vostry, P. [1 ]
Stulikova, I. [1 ]
Kiehn, J. [1 ]
Samatova, M. [1 ]
Kainer, K.U. [1 ]
Knoop, F.M. [1 ]
机构：
[1] Charles Univ, Prague, Czech Republic
来源：
Materials Science Forum | 1996年 / 210-213卷 / pt 2期
关键词：
Annealing - Atomization - Electric conductivity measurement - Fiber reinforced metals - Hardness - Metal extrusion - Metallic matrix composites - Strengthening (metal) - Thermodynamic stability;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Specimens of the microcrystalline commercial alloy WE 54 were prepared by gas atomization and by following extrusion at 250°C or 400°C. Their thermal stability was studied by isochronal annealing from room temperature up to 500°C by means of electrical resistivity and microhardness measurements. The results were compared to the results obtained on conventionally prepared WE 54 alloy and explained by precipitation effects. Specimens of the commercial alloy QE 22 and cp-Mg were reinforced by 22 vol% Saffil short fibres, exposed to the normalization heat treatment T4 and isochronally annealed up to 300°C. The annealing response of electrical resistivity was measured and compared to the annealing response of non-reinforced materials. The results show only a slight influence of strengthening fibres on precipitation processes in QE 22 alloy.
引用
收藏
页码：635 / 642
相关论文
共 50 条
  • [1] Electrical resistometry of Mg-based microcrystalline alloys and Mg-based composites
    Vostry, P
    Stulikova, I
    Kiehn, J
    Samatova, M
    Kainer, KU
    Knoop, FM
    NONDESTRUCTIVE CHARACTERIZATION OF MATERIALS VII, PTS 1 AND 2, 1996, 210-2 : 635 - 642
  • [2] Bulk amorphous Mg-based alloys
    Pryds, NH
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 375 : 186 - 193
  • [3] Hydrogenation of nanocrystalline Mg-based alloys
    Zander, D
    Lyubenova, L
    Köster, U
    Klassen, T
    Dornheim, M
    MATERIALS AND TECHNOLOGY FOR HYDROGEN ECONOMY, 2004, 801 : 89 - 94
  • [4] Bulk amorphous Mg-based alloys
    Pryds, N.H.
    Materials Science and Engineering: A, 2004, 375-377 (1-2 SPEC. ISS.) : 186 - 193
  • [5] MG-BASED AMORPHOUS-ALLOYS
    INOUE, A
    MASUMOTO, T
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 173 (1-2): : 1 - 8
  • [6] Electrochemical Hydriding of Mg-Based Alloys
    Vojtech, Dalibor
    Knotek, Vitezslav
    Novak, Pavel
    DIFFUSION IN SOLIDS AND LIQUIDS VI, PTS 1 AND 2, 2011, 312-315 : 882 - 887
  • [7] Current progresses in bulk Mg-based amorphous alloys and their composites
    College of Material Science and Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China
    Cailiao Gongcheng, 2008, 11 (75-79):
  • [8] Hydrogen Storage in Mg and Mg-Based Alloys and Composites Processed by Severe Plastic Deformation
    Leiva, D. R.
    Jorge, A. M., Jr.
    Ishikawa, T. T.
    Botta, W. J.
    MATERIALS TRANSACTIONS, 2019, 60 (08) : 1561 - 1570
  • [9] Hydrogenation of amorphous and nanocrystalline Mg-based alloys
    Spassov, T
    Köster, U
    JOURNAL OF ALLOYS AND COMPOUNDS, 1999, 287 (1-2) : 243 - 250
  • [10] Modeling of precipitation hardening in Mg-based alloys
    Katsman, Alexander
    Cohen, Shalom
    Bamberger, Menachem
    JOURNAL OF MATERIALS SCIENCE, 2007, 42 (16) : 6996 - 7003
12345