High temperature hot ductility of the 08Kh18N10T steel and its electroslag welded joint

被引：0
|
作者：
Astaf'ev, A.A.
Lepekhina, L.I.
Batieva, N.M.
Viktorov, N.A.
机构：
来源：
Tyazheloe Mashinostroenie | 1992年 / 12期
关键词：
Facilities - High temperature effects - Nuclear reactors - Plasticity testing - Stainless steel - Stamping - Steel analysis - Welds;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The 08Kh18N10T steel is widely used by the ATOMMASH Industrial corporation for the NPP pieces bottoms manufacture. Investigation results have been presented, which include hot ductility of the above steel and its welded joints made by the electroslag welding. Samples were tested for rapture within the 1050-700°C temperature range. For this steel and its welded joints dependence of reduction of area on temperature as well as fracture structure have been given. It has been shown that at 950-100° welded joint hot ductility is 3 times lower as compared to the basic metal. but at 700°C it increases by 3 times. So bottoms are recommended to be manufactured of 08Kh18N10T steel at 700-750°C.
引用
收藏
页码：30 / 33
相关论文
共 50 条
  • [1] HOT DUCTILITY OF STEEL 08KH18N10T
    Viktorov, N. A.
    METAL SCIENCE AND HEAT TREATMENT, 2011, 53 (5-6) : 263 - 264
  • [2] Hot ductility of steel 08Kh18N10T
    N. A. Viktorov
    Metal Science and Heat Treatment, 2011, 53 : 263 - 264
  • [3] 08KH18N10T STEEL ELECTROSLAG WELDED WITH DIRECT-CURRENT
    KRITSKII, MV
    LEPKHINA, LI
    BATIEVA, NM
    AUTOMATIC WELDING USSR, 1985, 38 (04): : 57 - 58
  • [4] Analysis of the structure of 08Kh18N10T welded joint
    Apasov, A.M.
    Kozlov, E.V.
    Apasov, A.A.
    Metallovedenie i Termicheskaya Obrabotka Metallov, 2001, (12): : 19 - 22
  • [5] MANUFACTURING TECHNOLOGY CENTRIFUGAL ELECTROSLAG CASTING FOR 08Kh18N10T STEEL
    Zherebtsov, S. N.
    Fat'yanov, S. V.
    CHEMICAL AND PETROLEUM ENGINEERING, 2006, 42 (1-2) : 114 - 116
  • [6] Low-cycle fatigue of welded joints of 08Kh18N10T steel
    Timofeev, B. T.
    Bazaras, Zh. L.
    MATERIALS SCIENCE, 2007, 43 (01) : 117 - 123
  • [7] Low-cycle fatigue of welded joints of 08Kh18N10T steel
    B. T. Timofeev
    Zh. L. Bazaras
    Materials Science, 2007, 43 : 117 - 123
  • [8] Viscoplastic Model for the Strain Resistance of 08Kh18N10T Steel at a Hot-Deformation Temperature
    Konovalov, A. V.
    Smirnov, A. S.
    RUSSIAN METALLURGY, 2008, (02): : 138 - 141
  • [9] Analysis of the weld structure for steel 08Kh18N10T
    Apasov, AM
    Kozlov, ÉV
    Apasov, AA
    METAL SCIENCE AND HEAT TREATMENT, 2001, 43 (11-12) : 489 - 492
  • [10] PROPERTIES OF STEEL 08KH18N10T IN A HELIUM ATMOSPHERE
    RYABCHENKOV, AV
    KUZNETSOV, EV
    MAKSIMOV, AI
    METAL SCIENCE AND HEAT TREATMENT, 1977, 19 (11-1) : 943 - 946
12345