Water-soluble sulfonated amino-formaldehyde resins. IV. Melamine-urea resins: synthesis and properties

被引:0
|
作者
机构
[1] Hovakeemian, George
[2] Absi-Halabi, Ma'mun
[3] Lahalih, Shawqui M.
来源
Hovakeemian, George | 1600年 / 38期
关键词
Concrete--Physical Properties - Plasticizers - Polymers--Molecular Weight;
D O I
暂无
中图分类号
学科分类号
摘要
The factors affecting the preparation and the properties of sulfonated melamine urea-formaldehyde resins were studied. The resins were synthesized using a four-step procedure previously used in preparing sulfonated melamine formaldehyde resins. The melamine-urea resins required higher hydroxymethylation and condensation temperatures as the percentage of urea increased. The molecular weight distribution of the prepared resins revealed the formation of low molecular weight species in increasing amounts with higher percentages of urea. The effectiveness of the prepared resins as dispersants for concrete mixes was found to be lower than the pure melamine resins; however, it was possible to enhance them by raising the ratio of sulfonated groups in the resins.
引用
收藏
相关论文
共 50 条
  • [41] Effects of synthesis method, melamine content and GPC parameter on the molecular weight of melamine-urea-formaldehyde resins
    Kim M.
    Park B.-D.
    Journal of the Korean Wood Science and Technology, 2021, 49 (01): : 1 - 13
  • [42] Synthesis and the effects of water-soluble sulfonated acetone-formaldehyde resin on the properties of concrete
    Pei, MS
    Yang, YQ
    Zhang, XZ
    Zhang, J
    Dong, JJ
    CEMENT AND CONCRETE RESEARCH, 2004, 34 (08) : 1417 - 1420
  • [43] Effects of urea formaldehyde resin to film properties of alkyd-melamine formaldehyde resins containing organo clay
    Bal, Ayca
    Guclu, Gamze
    Acar, Isil
    Iyim, Tuelin Banu
    PROGRESS IN ORGANIC COATINGS, 2010, 68 (04) : 363 - 365
  • [44] Synthesis of Polyurethane Resins Containing Water-Soluble Cellulose Derivatives
    Matsui, Eiki
    Sakamoto, Tasuku
    Fujita, Kanako
    Noorfarahin, Binti Rusly
    KOBUNSHI RONBUNSHU, 2012, 69 (11) : 646 - 650
  • [45] MELAMINE RESINS, A NEW CLASS OF WATER-SOLUBLE EMBEDDING MEDIA FOR ELECTRON-MICROSCOPY
    BACHHUBER, K
    FROSCH, D
    JOURNAL OF MICROSCOPY, 1983, 130 (APR) : 1 - 9
  • [46] Effect of synthesis method and melamine content of melamine-urea-formaldehyde resins on bond-line features in plywood
    Lubis M.A.R.
    Jeong B.
    Park B.-D.
    Lee S.-M.
    Kang E.-C.
    Journal of the Korean Wood Science and Technology, 2019, 47 (05): : 579 - 586
  • [47] Synthesis and properties of high-performance and good water-soluble melamine-formaldehyde resin
    Su, LH
    Qiao, SR
    Xiao, J
    Tang, X
    Zhao, GD
    Fu, SW
    JOURNAL OF APPLIED POLYMER SCIENCE, 2001, 81 (13) : 3268 - 3271
  • [48] The fire-retardant properties of the melamine-modified urea–formaldehyde resins mixed with ammonium polyphosphate
    Xing-Xia Ma
    Yu-Zhang Wu
    Hai-Long Zhu
    Journal of Wood Science, 2013, 59 : 419 - 425
  • [49] The effects of adding melamine at different resin synthesis points of low mole ratio urea-melamine-formaldehyde (UMF) resins
    College of Forestry, Shandong Agriculture University, 271018, Taian, China
    不详
    BioResour., 2013, 4 (5733-5748):
  • [50] SYNTHESIS AND CHARACTERIZATION OF WATER-SOLUBLE PHENOLIC RESINS AND ESTERS BASED ON CARDANOL
    RAO, GSS
    SRI, MR
    SHIRSALKAR, MM
    JOURNAL OF COATINGS TECHNOLOGY, 1986, 58 (738): : 55 - 63