Perpendicular magnetic anisotropy in NdFeB thin films

被引：0

作者：

Piramanayagam, S.N. ^{[1
]}

Matsumoto, M. ^{[1
]}

Morisako, A. ^{[1
]}

机构：

[1] Dept. of Information Engineering, Shinshu University, Nagano 380-8553, Japan

来源：

Journal of Applied Physics | 1999年 / 85卷 / 8 II B期

关键词：

Composition effects - Magnetic anisotropy - Neodymium compounds - Substrates - Thermal effects;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Nb2Fe14B thin films were analyzed based on perpendicular magnetic anisotropy (PMA). PMA was observed noted when films c axis was oriented perpendicularly to the film plane. Aside from the c-axis orientation, substrate composition and temperature were also found to contribute to the existence of PMA in NdFeB thin films. It was noted that an alteration in a substrate's composition and temperature prompts changes to occur on both the c-axis orientation and PMA.