Formation, microstructure and mechanical properties of Al-Fe base quasicrystalline alloys

被引：0

作者：

Kimura, H.M.

Sasamori, K.

Inoue, A.

机构：

来源：

Materials Science and Engineering A: Structural Materials: Properties, Microstructure and Processing | 2000年 / 294-296卷

关键词：

Quasicrystals - Ternary systems - Crystal microstructure - Strength of materials - High temperature properties - Aluminum powder metallurgy - Atomization - Powder metals - Decomposition - Phase composition - Melt spinning - Metal extrusion;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

An icosahedral (I) phase in coexistence with Al-phase was formed in the size fraction range up to 125 μm of atomized Al93Fe3Cr2Ti2 powder. The decomposition temperature of the I-phase is about 790 K. As per energy dispersive X-ray spectroscopy analysis, the constituent composition of the I-phase is Al84.2Fe7.0Cr6.3Ti2.5. It is found that the Al84.2Fe7.0Cr6.3Ti2.5 alloy forms a mostly single I-phase in the melt-spun state. Bulk I-alloys in a rod form were produced by extrusion of the atomized powders at 673 K and an extrusion ratio of 10. The extruded Al93Fe3Cr2Ti2 alloys have good mechanical properties, i.e., σ0.2 of 550 MPa, σUTS of 660 MPa and εp of 4.5% at room temperature and σ0.2 of 330 MPa, σUTS of 350 MPa and εp of 1.5% at 573 K. The I-based Al93Fe3Cr2Ti2 alloy is expected to be useful as a new type of high-elevated temperature strength material.

引用

页码：168 / 172