CHEMISTRY, MICROSTRUCTURE, AND TENSILE STRENGTH OF INGOT MOULDS.

被引：0

作者：

Sharma, S.K. ^{[1
]}

机构：

[1] Bethlehem Steel Corp, Primary, Processes Research Dep, Bethlehem,, PA, USA, Bethlehem Steel Corp, Primary Processes Research Dep, Bethlehem, PA, USA

来源：

Ironmaking and Steelmaking | 1984年 / 11卷 / 04期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

In contrast to other investigations, this work showed no relationship between the as-cast ferrite content and mold life. However, the ferrite content is largely controlled by the Si/Mn ratio. The tensile strength was low at room temperature and decreased at elevated temperatures.

引用

页码：214 / 226

共 50 条

[11] REFRACTORY COATINGS FOR SAND MOULDS.
Nail, C.C.
Situnayake, S.P.
Foundry Trade Journal, 1987, 161 (3344): : 177 - 178
[12] IMPROVE YOUR COSTING OF MOULDS.
Evans, Colin W.
1600, (165):
[13] Article on the development of ship moulds.
Weinblum, G
ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1932, 76 : 1149 - 1154
[14] HEATING/COOLING OF INJECTION MOULDS.
Friel, Peter
Kunststoffe - German Plastics, 1985, 75 (09): : 23 - 24
[15] CENTRIFUGAL CASTING IN SILICONE MOULDS.
Cox, Alison
Tin and Its Uses, 1986, (148): : 15 - 17
[16] SHORTENING HOLDING TIME OF INGOTS IN MOULDS.
Zal'tsman, E.S.
Klyuev, M.M.
Petrukhin, V.N.
1978, 8 (11): : 623 - 627
[17] PULL-OFF DEVICE FOR INJECTION MOULDS.
Sors, L.
Kunststoffe - German Plastics, 1980, 70 (07):
[18] Manufacture of concrete walls without the use of moulds.
不详
ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1921, 65 : 777 - 778
[19] Cold-injection moulding of aluminium moulds.
Zimmermann, F
ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1936, 80 : 132 - 133
[20] Aluminum diffusion protection for copper anode moulds.
Riccardi, J
Park, A
ELECTROREFINING AND ELECTROWINNING OF COPPER, 1999, : 379 - 382

← 1 2 3 4 5 →