Equilibrating partition ratios of Nb, Mn and Si between liquid iron and MgO-SiO2-MnO slag melts

被引：0

作者：

Tang, Zhonghe ^{[1
]}

Guo, Shangxing ^{[1
]}

Chen, Yongding ^{[1
]}

机构：

[1] Central Iron & Steel Research, Inst, China

来源：

Jinshu Xuebao/Acta Metallurgica Sinica | 1988年 / 24卷 / 05期

关键词：

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Liquid iron containing Nb, Mn and Si has been equilibrated with MgO-SiO2-MnO slag melts at 1600°C in a Mo wire wound resistance furnace with a duration of 4 hours. The oxygen activities in liquid iron were measured with oxygen sensors. Using the known equilibrium constants of the reactions and the oxygen activities in liquid iron, the component activities in the slag melts can be calculated. It was found that the partition ratios of Nb, Mn and Si have a close linear relationship with aFeO in a logarithmic scale. The dependence of Nb partition ratio on mole fractions of the slag components was also obtained.

引用

收藏

相关论文

共 50 条

[41] Review and modeling of viscosity of silicate melts:: Part II.: Viscosity of melts containing iron oxide in the CaO-MgO-MnO-FeO-Fe2O3-SiO2 system [J].

Zhang, L ;

Jahanshahi, S .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1998, 29 (01) :187-195

[42] EFFECTS OF CAO, MNO, AND AL2O3 ON PHOSPHORUS DISTRIBUTION BETWEEN LIQUID-IRON AND NA2O-MGO-FETO-SIO2 SLAGS [J].

KUNISADA, K ;

IWAI, H .

TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 27 (05) :332-339

[43] Thermodynamic behavior of manganese and phosphorus between liquid iron and CaO-MgO-SiO2-Al2O3-FetO-MnO-P2O5 slags [J].

Song, B ;

Kim, SH ;

Mao, JH ;

Lin, Q .

JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2001, 8 (03) :171-176

[44] Review and modeling of viscosity of silicate melts: Part II. viscosity of melts containing iron oxide in the CaO-MgO-MnO-FeO-Fe2O3-SiO2 system [J].

Ling Zhang ;

Sharie Jahanshahi .

Metallurgical and Materials Transactions B, 1998, 29 :187-195

[45] Thermodynamic behaviours of manganese and phosphorus between CaO-MgOsat-SiO2-Al2O3-FetO-MnO-P2O5 ladle slag and liquid iron [J].

Jung, IH ;

Seo, JD ;

Kim, SH .

STEEL RESEARCH, 2000, 71 (09) :333-339

[46] Effect of MgO on solidification crystallisation behaviour of high SiO2 content MnO-SiO2-Al2O3-based inclusions in Si-Mn-killed steel [J].

Lei, XuBo ;

Li, JianLi ;

Xu, Qi ;

Muvunyi, RodrigueArmel ;

Meng, YaoQing .

IRONMAKING & STEELMAKING, 2024,

[47] Wettability Between Si-Mn-Killed Steel and MgO-Based Refractory Containing SiO2 Impurities [J].

Cheng, Limei ;

Ren, Ying ;

Liu, Tingyao ;

Zhang, Lifeng .

STEEL RESEARCH INTERNATIONAL, 2022, 93 (05)

[48] RELATIONSHIP BETWEEN THE CALCULATED OXYGEN ACTIVITY AND THE SULFUR PARTITION RATIO FOR CaO-Al2O3-SiO2-MgO SLAG DURING LADLE REFINING [J].

Slovic, Zoran ;

Raic, Karlo T. ;

Nedeljkovic, Ljubomir ;

Volkov-Husovic, Tatjana .

MATERIALI IN TEHNOLOGIJE, 2012, 46 (06) :683-688

[49] Partition behavior of niobium between carbon saturated iron and slags from the CaO-Al2O3-SiO2-MgO system [J].

Bonnet, KD ;

Coley, KS .

60TH IRONMAKING CONFERENCE PROCEEDINGS, 2001, 60 :1223-1230

[50] Partition behavior of niobium between carbon saturated iron and slags from the CAO-AL2O3-SIO2-MGO system [J].

Bonnet, KD ;

Coley, KS .

84TH STEELMAKING CONFERENCE PROCEEDINGS, 2001, 84 :965-972

← 1 2 3 4 5 →