Characteristics of delamination in graphite/epoxy laminates under static and impact loads

被引：0

作者：

Kook, J.S. ^{[1
]}

Yang, I.Y. ^{[1
]}

Adachi, T. ^{[1
]}

机构：

[1] Daebul Univ, Chonnam, Korea, Republic of

来源：

Key Engineering Materials | 2000年 / 183卷

关键词：

Crack propagation - Delamination - Epoxy resins - Fractography - Fracture mechanics - Laminated composites - Scanning electron microscopy;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

In the present research, the characteristics of delamination in graphite/epoxy laminates subjected to static and impact load are discussed by the method of fractography experimentally. At first, delaminations were developed by double cantilever beam (DCB) test and end-notch flexure (ENF) test for some kinds of laminates. Their fracture surfaces were observed by scanning electron microscope. The propagated orientation of the delamination could be specified from the patterns of fracture surface. Next, each static and impact load was applied to square laminates to generate ripwise delaminations known as the typical pattern of low velocity impact damage. Based on the pattern specified by DCB and ENF tests, the propagation of delaminations for both loads were identified. Then it is obtained that the delamination in static and impact can be explained by the propagation from the transverse crack and the sequential delamination mechanism respectively.

引用

共 50 条

[11] DYNAMIC DELAMINATION FRACTURE-TOUGHNESS OF A GRAPHITE EPOXY LAMINATE UNDER IMPACT
SUN, CT
GRADY, JE
COMPOSITES SCIENCE AND TECHNOLOGY, 1988, 31 (01) : 55 - 72
[12] Delamination onset in symmetric cross-ply laminates under static loads: Theory, numerics and experiments
Carraro, Paolo Andrea
Novello, Elisa
Quaresimin, Marino
Zappalorto, Michele
COMPOSITE STRUCTURES, 2017, 176 : 420 - 432
[13] Simulations of delamination propagation in composite laminates under static and low-velocity impact transverse loads using a new cohesive model
Hu, Ning
Zemba, Yutaka
Fukunaga, Hisao
FRONTIERS IN MATERIALS SCIENCE AND TECHNOLOGY, 2008, 32 : 137 - +
[14] Delamination threshold loads for low velocity impact on composite laminates
Schoeppner, GA
Abrate, S
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2000, 31 (09) : 903 - 915
[15] Static and fatigue behaviour of stitched graphite/epoxy composite laminates
Aymerich, F
Priolo, P
Sun, CT
COMPOSITES SCIENCE AND TECHNOLOGY, 2003, 63 (06) : 907 - 917
[16] STRESS-TIME-TEMPERATURE-HUMIDITY EFFECTS ON DELAMINATION OF GRAPHITE EPOXY LAMINATES
GARG, AC
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1986, 108 (01): : 57 - 62
[17] Transient response of graphite/epoxy and Kevlar/epoxy laminates subjected to impact
Cairns, Douglas S., 1600, (27):
[18] Ballistic impact behaviour of stitched graphite/epoxy laminates
Caprino, G.
Lopresto, V.
Santoro, D.
COMPOSITES SCIENCE AND TECHNOLOGY, 2007, 67 (3-4) : 325 - 335
[19] DESIGNING FOR TOLERANCE TO IMPACT DAMAGE AT FASTENER HOLES IN GRAPHITE EPOXY LAMINATES UNDER COMPRESSION
JANARDHANA, MN
BROWN, KC
JONES, R
THEORETICAL AND APPLIED FRACTURE MECHANICS, 1986, 5 (01) : 51 - 55
[20] High performance estimations of delamination of graphite/epoxy laminates with electric resistance change method
Todoroki, A
Tanaka, M
Shimamura, Y
COMPOSITES SCIENCE AND TECHNOLOGY, 2003, 63 (13) : 1911 - 1920

← 1 2 3 4 5 →