SURFACE TEXTURES OF ANNEALED AISI 304 STAINLESS STEEL ETCHED BY AQUEOUS FERRIC CHLORIDE-HYDROCHLORIC ACID SOLUTIONS.

被引：0
|
作者：
Allen, D.M.
Hegarty, A.J.
Horne, D.F.
机构：
来源：
Transactions of the Institute of Metal Finishing | 1981年 / 59卷 / pt 1期
关键词：
D O I：
10.1080/00202967.1981.11870556
中图分类号：
学科分类号：
摘要：
The surface texture of the etched steel is strongly dependent on etchant composition and temperature. Optimum etching conditions have been found for achieving smooth and rough finishes. The role of the reaction products is also discussed.
引用
收藏
页码：25 / 29
相关论文
共 50 条
  • [41] Effect of surface machining and cold working on the ambient temperature chloride stress corrosion cracking susceptibility of AISI 304L stainless steel
    Ghosh, Swati
    Kain, Vivekanand
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (03): : 679 - 683
  • [42] STRESS-CORROSION CRACKING OF ANNEALED AND SENSITIZED TYPE-304 STAINLESS-STEEL IN DEAERATED CHLORIDE-SULFATE SOLUTIONS AT 290 C
    POZNANSKY, A
    DUQUETTE, DJ
    CORROSION, 1983, 39 (11) : 425 - 431
  • [43] STRESS-CORROSION CRACKING OF AISI 304 STAINLESS-STEEL IN CHLORIDE CONTAINING AMMONIUM-SULFATE SOLUTIONS AT 220-DEGREES-F
    TONG, HS
    SWARTZ, DJ
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1979, 126 (03) : C111 - C111
  • [44] STRESS-CORROSION CRACKING OF SENSITIZED AISI-304 STAINLESS-STEEL IN AQUEOUS CHLORIDE SOLUTIONS CONTAINING SULFUR SPECIES AT 50-C THROUGH 200-C
    LEE, JK
    SZKLARSKASMIALOWSKA, Z
    CORROSION, 1988, 44 (08) : 560 - 565
  • [45] Fractal and multifractal analysis of electrochemical noise to corrosion evaluation in A36 steel and AISI 304 stainless steel exposed to MEA-CO2 aqueous solutions
    Ramirez-Platas, Mariana
    Morales-Cabrera, Miguel A.
    Rivera, Victor M.
    Morales-Zarate, Epifanio
    Hernandez-Martinez, Eliseo
    CHAOS SOLITONS & FRACTALS, 2021, 145
  • [46] Enhanced localized and uniform corrosion resistances of bulk nanocrystalline 304 stainless steel in high-concentration hydrochloric acid solutions at room temperature
    S.G.Wang
    M.Sun
    Y.H.Xu
    K.Long
    Z.D.Zhang
    JournalofMaterialsScience&Technology, 2018, 34 (12) : 2498 - 2506
  • [47] Enhanced localized and uniform corrosion resistances of bulk nanocrystalline 304 stainless steel in high-concentration hydrochloric acid solutions at room temperature
    Wang, S. G.
    Sun, M.
    Xu, Y. H.
    Long, K.
    Zhang, Z. D.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (12) : 2498 - 2506
  • [48] ELECTROCHEMICAL BEHAVIOUR OF STAINLESS STEEL AISI-304 COUPLED WITH PT, AU AND GRAPHITE IN CONCENTRATED NITRIC ACID SOLUTIONS (65 PERCENT IN WEIGHT)
    CASARINI, G
    COLONNA, C
    SONGA, T
    METALLURGIA ITALIANA, 1970, 62 (05): : 183 - &
  • [49] Open circuit potentials of metallic chromium and austenitic 304 stainless steel in aqueous sulphuric acid solution and the influence of chloride ions on them
    Jegdic, Bore
    Drazic, Dragutin M.
    Popic, Jovan P.
    CORROSION SCIENCE, 2008, 50 (05) : 1235 - 1244
  • [50] Corrosion resistance of 304 stainless steel after anodic polarization in choline chloride-oxalic acid non-aqueous bath
    Winiarski, Juliusz
    Marczewski, Marek
    Tylus, Wlodzimierz
    OCHRONA PRZED KOROZJA, 2019, 62 (03): : 78 - 81
12345