OBSERVATION OF EXPLODED OR CHUNKY GRAPHITE PRECIPITATED IN THE REGION OF HIGH SILICON SEGREGATION IN SPHEROIDAL GRAPHITE CAST IRON.

被引：0

作者：

Tsutsumi, Nobuhisa

Imamura, Masato

机构：

来源：

Report of the Castings Research Laboratory, Waseda University | 1979年 / 30期

关键词：

Compendex;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

CAST IRON

引用

页码：55 / 60

共 12 条

[1] GRAPHITE MORPHOLOGY CONTROL IN CAST IRON.
Subramanian, S.V.
Ghosh, Debu
Kay, D.Alan R.
Purdy, Gary R.
I & SM, 1980, 7 (03): : 18 - 25
[2] COMPARISON OF MECHANICAL PROPERTIES OF CAST IRON WITH SPHEROIDAL GRAPHITE AND MAGNESIUM-TREATED MALLEABLE IRON.
Lepand, H.
Komp, V.
Jahnkow, H.
International cast metals journal, 1980, 5 (01): : 60 - 65
[3] GRAPHITE FORMATION PROCESSES IN SYNTHETIC CAST IRON.
Kogan, L.B.
Ivakhnenko, I.S.
1600,
[4] Effect of silicon and bismuth on solidification structure of thin wall spheroidal graphite cast iron
Department of Mechanical Engineering, School of Science and Engineering, Kinki University, Higashiosaka 577-8502, Japan
Mater. Trans., 1 (176-185):
[5] KINETICS OF SECOND STATE GRAPHITIZATION IN QUENCHED ALLOY SPHEROIDAL GRAPHITE IRON.
Chakrabarti, A.K.
Das, P.P.
British Foundryman, 1974, 67 (Part 12): : 330 - 334
[6] INFLUENCE OF SULFUR ON DISSOLVING BEHAVIOURS OF GRAPHITE IN MOLTEN CAST IRON.
Kayama, Nobutaro
Suzuki, Katsumi
Report of the Castings Research Laboratory, Waseda University, 1979, (30): : 61 - 67
[7] EFFECTS OF SULFUR ON THE NUCLEATION AND GROWTH OF GRAPHITE OUT OF RESIDUAL GRAPHITE PARTICLES IN MOLTEN CAST IRON.
Kayama, Nobutaro
Suzuki, Katsumi
Report of the Castings Research Laboratory, Waseda University, 1981, (32): : 25 - 31
[8] Twelfth Annual Summary of Recent Literature on Nodular Graphite Cast Iron.
Wolters, Diether
Giesserei, 1975, 62 (15): : 404 - 415
[9] EFFECT OF INDUCTION HEATING RATE ON THE QUENCH HARDNESS OF CAST IRON WITH SPHEROIDAL GRAPHITE.
Kolyada, V.A.
Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka Metallov), 1980, 22 (3-4): : 295 - 296
[10] Solidification and Shrinkage Cavity Formation of Austenitic Flake or Nodular Graphite Cast Irons in Comparison with Unalloyed Cast Iron.
Engler, Siegfried
Dette, Manfred
Giesserei, 1974, 61 (04): : 69 - 75

← 1 2 →