STRUCTURE OF PACKET MARTENSITE AND LOCALIZATION OF RETAINED AUSTENITE IN ENGINEERING STEEL.

被引：0
|
作者：
Eterashvili, T.V.
Utevskiy, L.M.
Spasskiy, M.N.
机构：
来源：
Physics of Metals and Metallography | 1979年 / 48卷 / 04期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
In low-carbon martensitic steel electron microscopic analysis has revealed neighboring parallel laths in four different combinations of orientation within a single zone of the martensite packet. Two types of combination cannot have long-range stress fields resulting from macrostrains during transformation. Layers of retained austenite are observed between the laths and packets after quenching, but not on the boundaries of the original austenite grains or on coherent twin boundaries.
引用
收藏
页码：113 / 121
相关论文
共 50 条
  • [21] ORIENTATION RELATIONSHIPS BETWEEN RETAINED AUSTENITE AND LATH MARTENSITE
    RAO, BVN
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (05): : 645 - 648
  • [22] On the role of interlath retained austenite in the deformation of lath martensite
    Maresca, F.
    Kouznetsova, V. G.
    Geers, M. G. D.
    MODELLING AND SIMULATION IN MATERIALS SCIENCE AND ENGINEERING, 2014, 22 (04)
  • [23] Role of Martensite-Austenite Component of Bainitic Structure in Formation of Properties of Pipe Steel. 1. Effect of Parameters of TMT
    N. G. Kolbasnikov
    S. A. Kuzin
    V. S. Teteryatnikov
    N. V. Zhukov
    R. R. Adigamov
    M. S. Sakharov
    M. A. Matveev
    Metal Science and Heat Treatment, 2022, 64 : 71 - 79
  • [24] Role of Martensite-Austenite Component of Bainitic Structure in Formation of Properties of Pipe Steel. 1. Effect of Parameters of TMT
    Kolbasnikov, N. G.
    Kuzin, S. A.
    Teteryatnikov, V. S.
    Zhukov, N., V
    Adigamov, R. R.
    Sakharov, M. S.
    Matveev, M. A.
    METAL SCIENCE AND HEAT TREATMENT, 2022, 64 (1-2) : 71 - 79
  • [25] Interaction of hydrogen and retained austenite in bainite/martensite dual-phase high strength steel
    Gu, JL
    Chang, KD
    Fang, HS
    Yang, ZG
    Bai, BZ
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2004, 11 (01) : 42 - 46
  • [26] INTENSIFICATION OF THE TRANSITION OF RETAINED AUSTENITE TO MARTENSITE EFFECTED BY CHANGING THE STRESS STATE IN TRIP STEEL WIRES
    Wiewiorowska, S.
    Muskalski, Z.
    Ciepiela, W.
    ARCHIVES OF METALLURGY AND MATERIALS, 2015, 60 (04) : 2729 - 2731
  • [27] Interaction of Hydrogen and Retained Austenite in Bainite/Martensite Dual-Phase High Strength Steel
    GU Jia-lin
    CHANG Kai-di
    FANG Hong-sheng
    YANG Zhi-gang
    BAI Bing-zhe
    Journal of Iron and Steel Research(International), 2004, 11 (01) : 42 - 46
  • [28] Investigations of residual stress distributions in retained austenite and martensite after carbonitriding of a low alloy steel
    Katemi, Richard J.
    Epp, Jeremy
    Hoffmann, Franz
    Steinbacher, Matthias
    RESIDUAL STRESSES IX, 2014, 996 : 550 - 555
  • [29] Response of ferrite, bainite, martensite, and retained austenite to a fire cycle in a fire-resistant steel
    Escobar, J. D.
    Delfino, P. M.
    Ariza-Echeverri, E. A.
    Carvalho, F. M.
    Schell, N.
    Stark, A.
    Rodrigues, T. A.
    Oliveira, J. P.
    Avila, J. A.
    Goldenstein, H.
    Tschiptschin, A. P.
    MATERIALS CHARACTERIZATION, 2021, 182 (182)
  • [30] INFLUENCE OF COOLING RATE ON THE MICROSTRUCTURE AND RETAINED AUSTENITE IN AN INTERCRITICALLY ANNEALED VANADIUM CONTAINING HSLA STEEL.
    BANGARU, NARASIMHA RAO V.
    SACHDEV, ANIL K.
    1982, 13 (N 11): : 1899 - 1906
12345