INFLUENCE OF AMORPHIZATION ON THE DISTRUBITUON OF BORON INTRODUCED INTO SILICON.

被引：0
|
作者：
Pistryak, V.M.
Tetel'baum, D.I.
Kozlov, V.F.
Vasil'ev, V.K.
Zorin, E.I.
Pavlov, P.V.
Fogel, Ya.M.
机构：
来源：
Soviet Physics, Semiconductors (English translation of Fizika i Tekhnika Poluprovodnikov) | 1974年 / 7卷 / 10期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The secondary ion - ion emission method was used in an investigation of the influence of a preliminary amorphization and subsequent annealing on the profile of boron implanted in silicon. The energy of boron ions was 100 keV. The preliminary amorphization was the result of bombardment with neon ions of 200 keV energy and 1000 mu C/cm**2 dose. Boron was implanted (500 mu C/cm**2) after a preliminary amorphization amd then silicon was annealed at temperatures below 550 degree C. The boron distribution profile was found to be narrower than in crystalline samples. When annealing was carried out at higher temperatures, the boron profile broadened considerably in the samples made amorphous by bombardment with neon ions. A significant broadening of the boron profile as a result of such annealing was not observed for crystalline samples which received similar boron doses. When the implanted boron dose was raised to 3000 mu C/cm**2, the boron profile broadened after annealing at temperatures above 600 degree C even in the samples which were not subjected to a preliminary amorphization. The observed behavior could be explained by an acceleration of the diffusion of boron as a result of formation of a large number of vacancies in the course of crystallization of an amorphous layer.
引用
收藏
页码：1325 / 1327
相关论文
共 50 条
  • [31] SUBMICRON CHANNEL MOSFET USING FOCUSED BORON ION BEAM IMPLANTATION INTO SILICON.
    Shukuri, Shoji
    Wada, Yasuo
    Masuda, Hiroo
    Ishitani, Tohru
    Tamura, Masao
    1600, (23):
  • [32] ELECTRICAL PROPERTIES OF FOCUSED-ION-BEAM BORON-IMPLANTED SILICON.
    Tamura, Masao
    Shukuri, Shoji
    Tachi, Shinichi
    Ishitani, Tohru
    Tamura, Hifumi
    1600, (22):
  • [33] Simulation on Boron Concentration Profile in Silicon Introduced by Plasma Doping
    Yu, Min
    Ji, Huihui
    Wang, Jinyan
    Jin, Yufeng
    Huang, Ru
    Zhang, Xing
    IEEE TRANSACTIONS ON PLASMA SCIENCE, 2010, 38 (09) : 2353 - 2358
  • [34] INFLUENCE OF OXYGEN ON RADIATION-STIMULATED DIFFUSION OF PHOSPHORUS IN SILICON.
    Borisenko, V.E.
    Buiko, L.D.
    Labunov, V.A.
    Ukhov, V.A.
    Soviet physics. Semiconductors, 1981, 15 (01): : 1 - 3
  • [35] INFLUENCE OF DEPOSITION CONDITIONS ON SPUTTER-DEPOSITED AMORPHOUS SILICON.
    Pawlewicz, W.T.
    1600, (49):
  • [36] INFLUENCE OF LASER RADIATION ON THE STATE OF A SOLID SOLUTION OF IRON IN SILICON.
    Zolotukhin, A.A.
    Ivanov, L.I.
    Milevskii, L.S.
    Prutskov, E.G.
    Yanushkevich, V.A.
    Soviet Journal of Quantum Electronics (English translation of Kvantovaya Elektronika), 1975, 5 (02): : 240 - 241
  • [37] On the influence of the chemical bond on the K a(1),(2)-doublet of silicon.
    Johnson, Nils G.
    ZEITSCHRIFT FUR PHYSIK, 1935, 95 (1-2): : 93 - 96
  • [38] INFLUENCE OF THE ORIENTATION OF THE ELECTRIC FIELD ON THE POLARIZATION DEPENDENCE OF THE ELECTROABSORPTION IN SILICON.
    Gutkin, A.A.
    Nasledov, D.N.
    Faradzhev, F.E.
    1600, (08):
  • [39] INFLUENCE OF GROWTH RATE ON THE IMPURITY CLOUD PARAMETERS IN PURE SILICON.
    Zabolotskii, S.E.
    Kalinushkin, V.P.
    Murina, T.M.
    Ploppa, M.G.
    Tempelhoff, K.
    1600, (88):
  • [40] Effect of amorphization and carbon co-doping on activation and diffusion of boron in silicon
    Pawlak, B. J.
    Janssens, T.
    Brijs, B.
    Vandervorst, W.
    Collart, E. J. H.
    Felch, S. B.
    Cowern, N. E. B.
    APPLIED PHYSICS LETTERS, 2006, 89 (06)
12345