Ultrafine-grained treatment process on FGH4096 alloy

被引：3

作者：

Ning, Yongquan ^{[1
]}

Yao, Zekun ^{[1
]}

Guo, Hongzhen ^{[1
]}

Tao, Yu ^{[2
]}

Zhang, Yiwen ^{[2
]}

机构：

[1] College of Materials Science and Engineering, Northwestern Polytechnical University, Xi'An

[2] High Temperature Materials Research Institute, China Iron and Steel Research Institute Group

来源：

Key Engineering Materials | 2009年 / 407-408卷

关键词：

Dual-property turbine disc; Mechanical properties; Multiple forging; Ultrafine grain;

D O I：

10.4028/www.scientific.net/KEM.407-408.694

中图分类号：

学科分类号：

摘要：

Ultrafine-grained treatment (multiple forging and heat treatment) were carried out on FGH4096 alloy to get ultrafine grain with grain being of 1-5iμm. OM, SEM, TEM and tensile test were used to study the action of ultrafine-grained treatment on improving structure and properties. The tensile properties of the alloy processed under ultrafine-grained treated have shown quite satisfactory levels, which ultimate strength (UTS) reach 1730Mpa and yield strength (YS) values reach 1470Mpa at room temperature. The apperance of advanced strength has originated chiefly form not only the persence of fine grains, but also structure of grain boundaries and diaperce pricipitations of secondary phase. A better combination of mechanical properties achieved by use of ultrafine-grained treatment makes it possible to explore the dual property turbine disc to its maximum potential for FGH 4096 alloy. © (2009) Trans Tech Publications, Switzerland.

引用

页码：694 / 697

页数：3

共 6 条

[1] Wlodek S.T., Kelly M., Alden M., Superalloy, (1996)
[2] Viswanathan G.B., Sarosia P.M., Whitis D.H., Et al., Deformation mechanisms at intermediate creep temperatures Ni-base superalloy Rene 88 DT, Materials Science and Engineering A, 400-401, pp. 489-495, (2005)
[3] Viswanathan G.B., Sarosia P.M., Henry M.F., Et al., Investigation of creep deformation mechanisms at intermediate temperatures in Rene 88 DT, Acta Materialia 53, pp. 3041-3057, (2005)
[4] Tsuda O., Kanamaru N., Furutaa S., Et al., PM nickel-base superalloy dual-property disks produced by superplastic forging, Metal Powder Report, 46, 3, pp. 31-35, (1991)
[5] Su Z., Yao Z., Guo H., Et al., New process for TC11 Ti alloy dual property disk, Acta Metallurgica Sinica (in Chinese), 32, 4, pp. 377-381, (1996)
[6] Yao Z., Guo H., Liu J., Etal. Forging mechanism of two-phase Ti-alloy compressor dsic with dual-property, The Chinese Journal of Nonferrous Metals (in Chinese), 10, 3, pp. 378-382, (2000)

← 1 →