Different damaged shaft lining concrete resistance to sulfate corrosion

被引：0

作者：

Li, Xurong ^{[1
]}

Ji, Hongguang ^{[1
]}

Liu, Juanhong ^{[1
]}

You, Shuang ^{[1
]}

机构：

[1] School of Civil and Environmental Engineering, University of Science and Technology Beijing, Beijing

来源：

Open Construction and Building Technology Journal | 2015年 / 8卷

关键词：

Concrete; Damage; Sulfate;

D O I：

10.2174/1874836801408010377

中图分类号：

学科分类号：

摘要：

Shaft lining concrete itself has a certain degree of initial damage before being corroded by sulfate. In order to study the resistance of the concrete of the initial damage in different corrosion solution concentration of sulfate, samples of concrete without initial damage, loaded 50% ultimate load and loaded 70% ultimate load with initial damage concrete were selected and studied their corrosion resistance in 9%, 12% and 15% concentrations of sulfate solution. The results show that compared with concrete with no initial damage, the concrete with initial damage resistance to sulfate corrosion is varied. With the increased concentration of the corrosion solution, the concrete with worse initial damage exhibited much lower resistance to sulfate corrosion. © Li et al.; Licensee Bentham Open.

引用

页码：377 / 381

页数：4

共 8 条

[1]

Teng H., Huang F., Ma D., Discussion on Durability of Concrete Exposed to Functions of Multiple Factors Containing Sulfate, Arch. Technol, 41, 9, pp. 834-836, (2010)

[2]

Zuo X., Sun W., Full process analysis of damage and failure of concrete subjected to external sulfate attack, J. Chinese Ceramic Soci, 37, 7, pp. 1063-1067, (2009)

[3]

Monteiro P., Kurtis K.E., Time to failure for concrete exposed to severe sulfate attack, Cem. Conc. Res, 33, 7, pp. 987-993, (2003)

[4]

Marchand J., Samsona E., Maltaisa Y., Theoretical Analysis of the Effect of Weak Sodium Sulfate Solution the Durability of Concrete, Cem. Conc. Composit, 24, 4, pp. 317-329, (2002)

[5]

Jin Z., Sun W., Zhang Y.S., Damage of Concrete in Sulfate and Chloride Solution, J. Chin. Ceramic Soc, 34, 5, pp. 630-635, (2006)

[6]

Liang Y., Yuan Y., Mechanism of concrete destruction under sodium sulfate and magnesium sulfate solution, J. Chin. Ceramic Soci, 35, 4, pp. 504-508, (2007)

[7]

Guan B., Chen S., Li H., Sulfate corrosion life of cement concrete under fatigue load, J Build. Mat, 15, 3, pp. 395-398, (2012)

[8]

Xu H., Chen Z., Guo X., Physical and mechanical performance and influencing factors of high performance concrete under sulfate attack, J. China Coal Soc, 37, 2, pp. 217-220, (2012)

← 1 →