Oxidation behavior of γ/Mo2Ni3Si ternary metal silicide alloy

被引：0
|
作者：
Xu, Y.W. [1 ]
Wang, H.M. [1 ]
机构：
[1] Laboratory of Laser Materials Processing and Manufacturing, School of Materials Science and Engineering, BeiHang University, 37 Xueyuan Road, Beijing, 100083, China
来源：
Journal of Alloys and Compounds | 2008年 / 457卷 / 1-2期
关键词：
The oxidation behavior of Mo2Ni3Si based ternary metal silicide alloy toughened by small amount of nickel-base solid solution (γ) was investigated at 1173 K. The oxide scale was observed to have a duplex structure consisting of a top columnar NiO layer and an internal NiO-SiO2 mixed layer with continuous SiO2 formed at its base. The continuous SiO2 layer made a significant contribution to the low oxidation rate through preventing the diffusion of oxygen and Ni2+. While; the cracks existing in the oxide scale due to growth stress; thermal stress and volatilization of MoO3 provided rapid diffusion paths for oxygen and Ni2+ and deteriorated the alloy's oxidation resistance. © 2007 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：239 / 243
相关论文
共 50 条
  • [41] Elevated-temperature wear behaviors of NiMo/Mo2Ni3Si intermetallic "in situ" composites
    Gui, Yongliang
    Song, Chunyan
    Wang, Shuhuan
    Zhao, Dingguo
    JOURNAL OF MATERIALS RESEARCH, 2016, 31 (01) : 66 - 75
  • [42] Microstructure of laser-melted Co/Co3Mo2Si wear resistant ternary metal silicide alloys
    Liu, Y
    Li, A
    Zhang, LY
    Wang, HM
    RARE METAL MATERIALS AND ENGINEERING, 2005, 34 (10) : 1657 - 1660
  • [43] Microstructure and corrosion resistance of laser clad coating of Ni2Si/Ni3Si2 silicide alloy
    Wang, CM
    Cai, LX
    Wang, HM
    RARE METAL MATERIALS AND ENGINEERING, 2003, 32 (03) : 197 - 200
  • [44] 激光熔化沉积γ/Mo2Ni3Si金属硅化物合金的腐蚀行为
    徐亚伟
    王华明
    稀有金属材料与工程, 2007, (04) : 660 - 664
  • [45] The New Ternary Silicide ErCo3Si2
    Dzevenko, Mariya
    Bigun, Inna
    ZEITSCHRIFT FUR NATURFORSCHUNG SECTION B-A JOURNAL OF CHEMICAL SCIENCES, 2014, 69 (03): : 369 - 372
  • [46] Corrosion properties of a Cr13Ni5Si2-based metal silicide alloy
    Yuan, L.
    Wang, H. M.
    INTERMETALLICS, 2008, 16 (09) : 1149 - 1155
  • [47] Oxidation behavior of Ni-Mo-Si alloy coatings fabricated on carbon steel by laser cladding
    Liu, Jing
    Chen, Yu
    Zhang, Jian
    SURFACE & COATINGS TECHNOLOGY, 2019, 375 : 903 - 910
  • [48] Oxidation resistance of silicide coatings on Mo and TZM alloy
    Moskal, Grzegorz
    Witala, Bartosz
    Moscicki, Adrian
    Kalamarz, Piotr
    Supernak, Waclaw
    Niemiec, Dawid
    Wrona, Adriana
    Osadnik, Malgorzata
    OCHRONA PRZED KOROZJA, 2016, 59 (02): : 46 - 52
  • [49] High-temperature sliding wear resistance of a ductile metal-toughened Cr13Ni5Si2 ternary metal silicide alloy
    Fang, Y. L.
    Wang, H. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 433 (1-2) : 114 - 119
  • [50] Effect of Si solution in a-Mo on oxidation behavior of Mo-Si-B alloy and oxidation kinetics model
    Wang, Juan
    Zhang, Xiaojiao
    Zhang, Guojun
    Li, Bin
    Li, Rui
    Li, Shujuan
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2023, 116
12345