Oxidation behavior of γ/Mo2Ni3Si ternary metal silicide alloy

被引：0
|
作者：
Xu, Y.W. [1 ]
Wang, H.M. [1 ]
机构：
[1] Laboratory of Laser Materials Processing and Manufacturing, School of Materials Science and Engineering, BeiHang University, 37 Xueyuan Road, Beijing, 100083, China
来源：
Journal of Alloys and Compounds | 2008年 / 457卷 / 1-2期
关键词：
The oxidation behavior of Mo2Ni3Si based ternary metal silicide alloy toughened by small amount of nickel-base solid solution (γ) was investigated at 1173 K. The oxide scale was observed to have a duplex structure consisting of a top columnar NiO layer and an internal NiO-SiO2 mixed layer with continuous SiO2 formed at its base. The continuous SiO2 layer made a significant contribution to the low oxidation rate through preventing the diffusion of oxygen and Ni2+. While; the cracks existing in the oxide scale due to growth stress; thermal stress and volatilization of MoO3 provided rapid diffusion paths for oxygen and Ni2+ and deteriorated the alloy's oxidation resistance. © 2007 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：239 / 243
相关论文
共 50 条
  • [21] Microstructure and room-temperature dry sliding wear behavior of Mo2Ni3Si/γ dual-phase alloy
    Xu, Yawei
    Wang, Huaming
    Jinshu Xuebao/Acta Metallurgica Sinica, 2006, 42 (07): : 722 - 726
  • [22] Elevated temperature wear behaviors of a Co-Mo-Si ternary metal silicide alloy
    Liu, Y
    Wang, HM
    SCRIPTA MATERIALIA, 2005, 52 (12) : 1235 - 1240
  • [23] Characterization and oxidation behavior of silicide coating on multiphase Mo-Si-B alloy
    Tang, Zhihong
    Thom, Andrew J.
    Kramer, M. J.
    Akinc, Mufit
    INTERMETALLICS, 2008, 16 (09) : 1125 - 1133
  • [24] Corrosive sliding wear behavior of laser clad Mo2Ni3Si/NiSi intermetallic coating
    Lu, XD
    Wang, HM
    APPLIED SURFACE SCIENCE, 2005, 245 (1-4) : 346 - 352
  • [25] OXIDATION OF A NI-CR-MO TERNARY ALLOY
    MACKERT, JR
    PARRY, EE
    FAIRHURST, CW
    JOURNAL OF DENTAL RESEARCH, 1984, 63 : 234 - 234
  • [26] Microstructure and hot corrosion behaviors of a γ-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal silicide alloy
    Yuan, L.
    Wang, H.M.
    Journal of Alloys and Compounds, 2009, 479 (1-2): : 217 - 224
  • [27] Microstructure and hot corrosion behaviors of a γ-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal silicide alloy
    Yuan, L.
    Wang, H. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 479 (1-2) : 217 - 224
  • [28] A wear resistant ductile metal-toughened Cr13Ni5Si2 ternary metal silicide alloy
    Fang, YL
    Tang, HB
    Wang, HM
    INTERMETALLICS, 2006, 14 (07) : 750 - 758
  • [29] Dry Sliding Wear Resistance of NiMo/Mo2Ni3Si Intermetallic Composites
    Song, Chunyan
    Gui, Yongliang
    Hu, Binsheng
    Qi, Xuejing
    MATERIALS AND DESIGN, PTS 1-3, 2011, 284-286 : 65 - 68
  • [30] 凝固条件对γ-Ni/MO2Ni3Si合金凝固组织的影响
    徐亚伟
    王华明
    中国激光, 2007, (03) : 427 - 431
12345