Preparation and characterization of electrospun magnetic carbon composite nanofibres

被引：0

作者：

Tang, Ying-Mao ^{[1
]}

Miao, Qing-Qing ^{[2
]}

Xiao, Li-Ren ^{[1
]}

Qian, Qing-Rong ^{[2
]}

Chen, Qing-Hua ^{[2
]}

机构：

[1] College of Materials Science and Engineering, Fujian Normal University, Fuzhou,350007, China

[2] College of Environmental Science and Engineering, Fujian Normal University, Fuzhou,350007, China

来源：

Wuji Cailiao Xuebao/Journal of Inorganic Materials | 2014年 / 29卷 / 08期

关键词：

Nanomagnetics - Carbon nanofibers - Carbonization - Saturation magnetization - Magnetic properties - Carbon carbon composites - Nanoparticles;

D O I：

10.15541/jim20130577

中图分类号：

学科分类号：

摘要：

Magnetic carbon composite nanofibres, using the mixed homogeneous solution consist of polyacrylonitrile (PAN), ferric acetylacetonate (AAI) and dimetbylformamide (DMF) as raw material, were prepared by electrospinning-calcination technology. TEM analysis showed that the carbon nanofibre diameter of sample CF900 was about 130-210 nm, in which magnetic nanoparticles were uniformly distributed. The magnetic properties of carbon composite nanofibres under different carbonization temperature was also investigated. Results showed that saturation magnetization (Ms) and remanent magnetization (Mr) increased with the increase of the temperature. When carbonization temperature was 900℃, the sample was of good magnetic property with high saturation magnetization (Ms=27.55 A·m2/kg). Moreover, the specific surface area (SBET) and total pore volume (Vtotal) were up to 354.0 m2/g and 0.315 mL/g, respectively.

引用

页码：827 / 834

共 50 条

[31] Casein release and characterization of electrospun nanofibres for cartilage tissue engineering
Mehdi Movahedi
Amin Orash Mahmoud Salehi
Fatemeh Poodineh hajipour
Sina Etemad
Bulletin of Materials Science, 45
[32] Casein release and characterization of electrospun nanofibres for cartilage tissue engineering
Movahedi, Mehdi
Salehi, Amin Orash Mahmoud
Hajipour, Fatemeh Poodineh
Etemad, Sina
BULLETIN OF MATERIALS SCIENCE, 2022, 45 (02)
[33] Investigation of fundamental parameters affecting electrospun PVA/CuS composite nanofibres
Wang, C.
Yuan, J.
Niu, H.
Yan, E.
Zhao, H.
PIGMENT & RESIN TECHNOLOGY, 2009, 38 (01) : 25 - 32
[34] Recovery of critical metals from leach solution of electronic waste using magnetite electrospun carbon nanofibres composite
Aamir Iqbal
M. Rasul Jan
Jasmin Shah
Bahroz Rashid
Environmental Science and Pollution Research, 2022, 29 : 88763 - 88778
[35] Carbonized electrospun cellulose composite nanofibres containing silicon carbide nanoparticles
Li, Qiang
Zhu, Yanqiu
Eichhorn, Stephen J.
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2019, 123 : 71 - 78
[36] Electrospun composite nanofibres of PVA loaded with nanoencapsulated n-octadecane
Sirohi, Sidhharth
Singh, Dhirendra
Nain, Ratyakshi
Parida, Dambarudhar
Agrawal, Ashwini K.
Jassal, Manjeet
RSC ADVANCES, 2015, 5 (43): : 34377 - 34382
[37] Preparation and Characterization of Sodium Alginate-Polyvinyl Alcohol Electrospun Nanofibres Using Green Solvents for Biomedical Applications
Mathew, Jomit T. T.
Jose, E. Tomlal
Philip, Princy
Mohan, M. Gayathri
Cherian, Shijo K. K.
POLYMER SCIENCE SERIES A, 2022, 64 (06) : 724 - 732
[38] Preparation and Characterization of Sodium Alginate-Polyvinyl Alcohol Electrospun Nanofibres Using Green Solvents for Biomedical Applications
Jomit T. Mathew
Tomlal Jose E
Princy Philip
Gayathri Mohan M.
Shijo K. Cherian
Polymer Science, Series A, 2022, 64 : 724 - 732
[39] Preparation and Characterization of Electrospun PLGA/silver Composite Nanofibers for Biomedical Applications
Khalil, Khalil Abdelrazek
Fouad, H.
Elsarnagawy, T.
Almajhdi, Fahad N.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2013, 8 (03): : 3483 - 3493
[40] Preparation and characterization of a novel magnetic composite particles
Shang, Hongzhou
Zhang, Xin
Zhao, Jingdong
Liang, Hongyu
RUSSIAN JOURNAL OF APPLIED CHEMISTRY, 2015, 88 (03) : 529 - 532

← 1 2 3 4 5 →