Characterization for Water Vapor Sorption and Organic Content of Silane-impregnated Cement-Based Materials

被引：0
|
作者：
Jing W. [1 ]
Yang R. [2 ]
Li K. [1 ]
机构：
[1] Civil Engineering Department, Tsinghua University, Beijing
[2] Chemical Engineering Department, Tsinghua University, Beijing
来源：
Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society | 2020年 / 48卷 / 05期
关键词：
Cement-based materials; Pyrolysis-gas chromatography-mass spectrometry; Silane impregnation; Water vaporsorption/ desorption isotherm;
D O I：
10.14062/j.issn.0454-5648.2020.05.20190486
中图分类号：
学科分类号：
摘要：
Silane impregnation is commonly used as a durability protection measure for concrete. Cement-based materials impregnated with triethoxyisobutylsilane were analyzed by pyrolysis-gas chromatography-mass spectrometry (PGC-MS) to identify the characteristic structure and amount of impregnation. The main component of the pyrolysis fragments is isobutyl. The water vapor sorption isotherm (WVSI) was determined to investigate the interaction between moisture and the impregnated materials. There is no notable difference at a humidity of <30%, the pore condensation (adsorption) and "ink-bottle" effect (desorption) substantially decrease, and the adsorption/desorption rate increases due to the impregnation at a humidity of>60%. The Xenon lamp ageing (10 weeks) after laboratory accelerated ageing process does not change the silane content and the WVSI characteristics. © 2020, Editorial Department of Journal of the Chinese Ceramic Society. All right reserved.
引用
收藏
页码：675 / 681
页数：6
相关论文
共 22 条
  • [21] Wu M., Johannesson B., Geiker M., A study of the water vapor sorption isotherms of hardened cement pastes: Possible pore structure changes at low relative humidity and the impact of temperature on isotherms, Cem Concr Res, 56, pp. 97-105, (2014)
  • [22] Snoeck D., Velasco L.F., Mignon A., Et al., The influence of different drying techniques on the water sorption properties of cement-based materials, Cem Concr Res, 64, pp. 54-62, (2014)
123