Failure analysis of parietal cracking in scavenging pump made of die casting aluminium alloy

被引：0
|
作者：
Gong, Lei [1 ]
Fu, Ge-Yan [1 ]
机构：
[1] School of Mechanical and Electronic Engineering, Soochow University, Suzhou 215021, China
来源：
Jinshu Rechuli/Heat Treatment of Metals | 2006年 / 31卷 / 08期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Failure analysis of parietal cracking in scavenging pump made of die casting aluminium alloy was carried out by means of metallographic examination, SEM analysis and so on. The results show that the material defects including shrinkage porosity and needle structures resulting from non-normal die casting process or heat treatment are the main facts to cause the brittle fracture in parietal of the scavenging pump made of die casting aluminium alloy. Finally some improvement methods were put forward.
引用
收藏
页码：93 / 95
相关论文
共 50 条
  • [1] PREMATURE CRACKING OF DIES FOR ALUMINIUM ALLOY DIE-CASTING
    Pawlowski, B.
    Bala, P.
    Tokarski, T.
    Krawczyk, J.
    ARCHIVES OF METALLURGY AND MATERIALS, 2013, 58 (04) : 1275 - 1279
  • [2] Resistance of threadings made of aluminium alloy and fabricated by die casting in presence of casting defects
    Doglione, R.
    Metallurgia Italiana, 2019, 111 (09): : 39 - 50
  • [3] Failure analysis of aluminum alloy casting die made of H13 steel
    Liang, Si-Zu
    Liang, Yao-Neng
    Li, Mao-Ping
    Jinshu Rechuli/Heat Treatment of Metals, 2002, 27 (12):
  • [4] Thermal stresses in aluminium alloy die casting dies
    Klobcar, Damjan
    Tusek, Janez
    COMPUTATIONAL MATERIALS SCIENCE, 2008, 43 (04) : 1147 - 1154
  • [5] Mechanisms of die failure caused by die/casting soldering during high pressure die casting of aluminium alloys
    Chen, ZW
    PROCEEDINGS OF THE FOURTH INTERNATIONAL CONFERENCE ON MATERIALS ENGINEERING FOR RESOURCES, VOL 1, 2001, : 231 - 236
  • [6] Stress corrosion cracking failure of jackbolts for die casting press
    Manohar, P. A.
    THERMEC 2006, Pts 1-5, 2007, 539-543 : 2162 - 2167
  • [7] Damage analysis on the surface of die casting die of sirder made by aluminium allay of AlSi9Cu3
    Kosec, B
    Kosec, L
    Kopac, J
    Skrinjar, A
    STROJNISKI VESTNIK-JOURNAL OF MECHANICAL ENGINEERING, 2001, 47 (09): : 575 - 578
  • [8] Comparisons of Process Capability in Cold Chamber Die Casting of Aluminium Alloy
    Rupinder Singh
    Proceedings of the National Academy of Sciences, India Section A: Physical Sciences, 2018, 88 : 351 - 356
  • [9] The effects of scandium on A356 aluminium alloy in gravity die casting
    Lim, Y. P.
    Yeo, W. H.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 395 - 399
  • [10] Aging of maraging steel welds during aluminium alloy die casting
    Klobcar, D.
    Tusek, J.
    Taljat, B.
    Kosec, L.
    Pleterski, M.
    COMPUTATIONAL MATERIALS SCIENCE, 2008, 44 (02) : 515 - 522
12345