Styrene-assisted grafting of maleic anhydride onto deproteinized natural rubber

被引：0
|
作者：
机构：
[1] Wongthong, Pinyo
[2] Nakason, Charoen
[3] Pan, Qinmin
[4] Rempel, Garry L.
[5] 1,5,Kiatkamjornwong, Suda
来源：
Kiatkamjornwong, S. (ksuda@chula.ac.th) | 1600年 / Elsevier Ltd卷 / 59期
关键词：
Grafting of maleic anhydride (MA) onto deproteinized natural rubber (DPNR) was carried out using a differential microemulsion polymerization technique. To improve the grafting efficiency (G.E) and reduce the gel content in the grafts; deproteinizing the NR latex was conducted before the grafting reaction and styrene (ST) comonomer was used to increase the G.E. The effects of initiator and monomer concentration; reaction temperature; reaction time; monomer addition rate; and ST/MA ratio on G.E and gel content were investigated. Kinetics of grafting reaction in either the presence or absence of ST was investigated. The results showed that introduction of copolymerizing styrene could significantly improve both the G.E and the grafting content. The G.E increased with increasing ST/MA ratio. The optimal grafting condition was initiator and MA concentrations of 7 wt% and 9 wt% of dried rubber content; ST/MA mole ratio of 4:1; and MA addition rate of 0.6 ml/min at 60 °C for 4 h. The addition of styrene to the grafting process enhances the graft copolymerization rate of MA grafting onto DPNR. © 2014 Elsevier Ltd. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
12345