Comparative corrosion behavior of Alloys 690 and 800 in high-temperature water: Combined effects of polyacrylic acid and dissolved oxygen

被引：0

作者：

Zhang, Zhiyuan ^{[1
,2
,3
]}

Zhang, Zhiming ^{[3
]}

Wang, Jianqiu ^{[1
,2
,3
]}

Ming, Hongliang ^{[1
,2
]}

Zhu, Haipeng ^{[1
,2
]}

Han, En-Hou ^{[1
,3
,4
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China

[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China

[3] Inst Corros Sci & Technol, Guangzhou 510530, Peoples R China

[4] South China Univ Technol, Sch Mat Sci & Engn, Guangzhou 510006, Peoples R China

来源：

CORROSION SCIENCE | 2025年 / 245卷

关键词：

Polyacrylic acid; Alloy; 690; 800; High-temperature water; Dissolved oxygen; Oxide film; GRAIN-BOUNDARY-CHARACTER; OXIDE-FILM FORMATION; ELECTROCHEMICAL PROPERTIES; STAINLESS-STEELS; PH; MECHANISM; DEGRADATION;

D O I：

10.1016/j.corsci.2025.112709

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The corrosion behavior of Alloys 690 and 800 was investigated in high-temperature water containing dissolved oxygen (DO) and polyacrylic acid (PAA). DO caused Cr dissolution as HCrO4-, leading to the formation of Crdepleted oxide films on both alloys. Alloy 800, with higher Fe content, formed a more protective Ni-Fe spinel inner layer, while Alloy 690, with lower Fe content, formed a less protective NiO inner layer. The thermal degradation of PAA resulted in surface acidification, which accelerated Cr and Ni dissolution under DO, further intensifying corrosion. Under DO conditions, Alloy 800 exhibited superior oxidation resistance compared to Alloy 690, regardless of PAA presence.

引用

页数：13

共 57 条

[51]

Varrin RD, 2017, WOODHEAD PUBL SER EN, P323, DOI 10.1016/B978-0-08-100894-2.00013-3

[52] Comparison of Corrosion Resistance of UNS N06690TT and UNS N08800SN in Simulated Primary Water with Various Concentrations of Dissolved Oxygen [J].

Wang, Jianqiu ;

Li, Xiaohui ;

Huang, Fa ;

Zhang, Zhiming ;

Wang, Jiazhen ;

Staehle, Roger W. .

CORROSION, 2014, 70 (06) :598-614

[53] Assessing the influence of welding-induced mechanics on oxidation and stress corrosion cracking in an Alloy 600-Alloy 152 M weldment under simulated PWR primary water [J].

Xu, Xinhe ;

Pan, Deng ;

Li, Entong ;

Lu, Zhanpeng ;

Cui, Tongming ;

Chen, Junjie ;

Zheng, Hui ;

Li, Kai ;

Lozano-Perez, Sergio ;

Shoji, Tetsuo .

JOURNAL OF NUCLEAR MATERIALS, 2024, 601

[54] A three-dimensional nickel-chromium layered double hydroxide micro/nanosheet array as an efficient and stable bifunctional electrocatalyst for overall water splitting [J].

Ye, Wen ;

Fang, Xiaoyu ;

Chen, Xuebo ;

Yan, Dongpeng .

NANOSCALE, 2018, 10 (41) :19484-19491

[55] Influence of dissolved oxygen on oxide films of Alloy 690TT with different surface status in simulated primary water [J].

Zhang, Zhiming ;

Wang, Jianqiu ;

Han, En-Hou ;

Ke, Wei .

CORROSION SCIENCE, 2011, 53 (11) :3623-3635

[56] Effect of polyacrylic acid on the corrosion behavior of Alloy 690 in pressurized water reactor secondary water [J].

Zhang, Zhiyuan ;

Zhang, Zhiming ;

Wang, Jianqiu ;

Ming, Hongliang ;

Zhu, Haipeng ;

Dan, Tichun ;

Wang, Ruoyu ;

Gao, Beibei ;

Han, En-Hou .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2025, 220 :1-13

[57] Elucidating the interaction mechanisms between polyacrylic acid and Alloy 800 oxide films under pressurized water reactor steam generator conditions [J].

Zhang, Zhiyuan ;

Zhang, Zhiming ;

Wang, Jianqiu ;

Okonkwo, Bright O. ;

Zhu, Haipeng ;

Qu, Jiahui ;

Jiang, Yilan ;

Huang, Rongshen ;

Han, En-Hou .

CORROSION SCIENCE, 2024, 236

← 1 2 3 4 5 6 →