The role of cyclic oxidation on low cycle fatigue crack initiation and growth behaviour of a Ni-based superalloy

被引：1
作者：
Rai, R. K. [1 ]
机构：
[1] Malaviya Natl Inst Technol Jaipur, Jaipur 302017, Rajasthan, India
来源：
MATERIALS CHEMISTRY AND PHYSICS | 2025年 / 332卷
关键词：
Low cycle fatigue; TEM; Microstructure; Oxidation;
D O I：
10.1016/j.matchemphys.2024.130311
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Low cycle fatigue (LCF) resistance of Ni-based superalloys plays a pivotal role in optimizing the design and life of the turbine blades under oxidizing conditions. It is essential for ensuring long term reliability and structural integrity. In this study, the author presents experimental evidence of oxygen ingress during LCF deformation of directionally solidified (DS) CM 247 alloy at 850 degrees C, highlighting its detrimental effects on crack initiation and growth mechanisms. Compositional analysis revealed that the NiO, Cr2Os, and Al2Os oxide layers formed on the surface, which cracks during cyclic loading, leading to early crack initiation. Additionally, oxygen ingress through these cracks accelerates crack propagation. Early crack nucleation and accelerated crack growth contribute to a reduced LCF life.
引用
收藏
页数：5
相关论文
共 50 条
  • [1] The role of oxidation damage in fatigue crack initiation of an advanced Ni-based superalloy
    Cruchley, S.
    Li, H. Y.
    Evans, H. E.
    Bowen, P.
    Child, D. J.
    Hardy, M. C.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2015, 81 : 265 - 274
  • [2] Crack Initiation in Ni-Based Single Crystal Superalloy under Low-Cycle Fatigue-Oxidation Conditions
    Wang, Pengfei
    Zhao, Xinbao
    Yue, Quanzhao
    Xia, Wanshun
    Ding, Qingqing
    Bei, Hongbin
    Gu, Yuefeng
    Zhang, Ze
    [J]. METALS, 2023, 13 (11)
  • [3] Quantifying the impact of oxidized carbide expansion on fatigue crack initiation in a Ni-based single-crystal superalloy
    Zhou, Zaifeng
    Wang, Dekun
    Li, Runguang
    Wang, Youkang
    Jin, Xueyi
    Wang, Tianze
    Li, Tiancheng
    Li, Shilei
    Xie, Guang
    Zhang, Jian
    Wang, Yan-Dong
    [J]. MATERIALS CHARACTERIZATION, 2025, 220
  • [4] Crystallographic evaluation of low cycle fatigue crack growth in a polycrystalline Ni based superalloy
    Barat, Kaustav
    Ghosh, Abhijit
    Doharey, Alok
    Mukherjee, Shreya
    Karmakar, Anish
    [J]. INTERNATIONAL JOURNAL OF PLASTICITY, 2022, 149
  • [5] Effect of oxidation on the competition between internal and external fatigue crack initiation of Ni-based single crystal superalloy
    Meng, Yang
    Zhou, Chungen
    Zhao, Zihua
    Shen, Yuliang
    Pei, Haonan
    Zhao, Ming
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2025, 197
  • [6] Oxidation micromechanics and contribution during the low-cycle fatigue failure of a Ni-based single crystal superalloy
    Li, Y. M.
    Guo, H. Y.
    Wang, X. G.
    Tan, Z. H.
    Yang, Y. H.
    Du, Y. L.
    Liu, J. L.
    Liu, J. D.
    Zhou, Y. Z.
    Sun, X. F.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2025, 190
  • [7] Oxidation ahead of a crack tip in an advanced Ni-based superalloy
    Kitaguchi, H. S.
    Li, H. Y.
    Evans, H. E.
    Ding, R. G.
    Jones, I. P.
    Baxter, G.
    Bowen, P.
    [J]. ACTA MATERIALIA, 2013, 61 (06) : 1968 - 1981
  • [8] Effect of Notches on Fatigue Crack Initiation and Early Propagation Behaviors of a Ni-Based Superalloy at Elevated Temperatures
    Zhao, Zuopeng
    Hu, Xuteng
    Guo, Zhiwei
    [J]. METALS, 2025, 15 (04)
  • [9] Microstructure Evaluation and Low Cycle Fatigue Damage due to Degradation of Ni-based Superalloy
    Heo, Inkang
    Yoon, Donghyun
    Hong, Sanghyun
    Kim, Jinyeol
    Kim, Jaehoon
    Chang, Sungho
    Bae, Siyeon
    [J]. KOREAN JOURNAL OF METALS AND MATERIALS, 2018, 56 (08): : 561 - 569
  • [10] Experimental investigation on low cycle fatigue and fracture behaviour of a notched Ni-based superalloy at elevated temperature
    Yuan, S. H.
    Wang, Y. R.
    Wei, D. S.
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2014, 37 (09) : 1002 - 1012
12345