Compressive and thermal characterization of syntactic foams containing hollow silicon carbide particles with porous shell

被引：0
|
作者：
机构：
[1] Labella, Matthew
[2] Shunmugasamy, Vasanth Chakravarthy
[3] Strbik, Oliver M.
[4] Gupta, Nikhil
来源：
Gupta, N. (ngupta@nyu.edu) | 1600年 / John Wiley and Sons Inc卷 / 131期
关键词：
Silicon carbide hollow particle (SiCHS) reinforced vinyl ester matrix syntactic foams are prepared and characterized for compressive properties and coefficient of thermal expansion (CTE). Two types of SiCHS were utilized in 60 vol % to prepare syntactic foams. These SiCHS had ratio of inner to outer radius of 0.91 and 0.84 for the thin and thick walled particles. The specific compressive strength values were 33.4 and 38.8 kPa/kg/m3 and the specific compressive modulus values were 0.8 MPa/kg/m3 and 0.6 MPa/kg/m3 for the thin and thick walled SiCHS-filled syntactic foams; respectively. The shell of the hollow particles contained microporous voids; and the porosity was estimated as 16.6% and 24.8% in the walls of the thin and thick walled particles; respectively. The shell porosity adversely affected the specific compressive strength and the modulus of the syntactic foam. However; the SiCHS-filled syntactic foams exhibited low CTE values (26.7 and 15.9 × 10-6/°C). These CTE values were 65.1% and 79.3% lower than the CTE of the neat resin. Such properties can be useful for applications where syntactic foams are exposed to high temperatures and dimensional stability is important. A theoretical model is used to estimate the porosity level in the SiC shells and estimate the effective mechanical properties of the porous SiC material that forms the particle shell. Such analysis can help in using the models as predictive tools to estimate the mechanical properties of syntactic foams. © 2014 Wiley Periodicals; Inc; J; Appl; Polym; Sci; 2014; 131; 40689. Copyright © 2014 Wiley Periodicals;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Compressive and Thermal Characterization of Syntactic Foams Containing Hollow Silicon Carbide Particles with Porous Shell
    Labella, Matthew
    Shunmugasamy, Vasanth Chakravarthy
    Strbik, Oliver M., III
    Gupta, Nikhil
    JOURNAL OF APPLIED POLYMER SCIENCE, 2014, 131 (17) : 8593 - 8597
  • [2] Dynamic and Thermal Properties of Aluminum Alloy A356/Silicon Carbide Hollow Particle Syntactic Foams
    Cox, James
    Luong, Dung D.
    Shunmugasamy, Vasanth Chakravarthy
    Gupta, Nikhil
    Strbik, Oliver M., III
    Cho, Kyu
    METALS, 2014, 4 (04): : 530 - 548
  • [3] Microstructure and compressive properties of aluminum matrix syntactic foams containing Al2O3 hollow particles
    Rao, D. W.
    Yang, Y. W.
    Huang, Y.
    Sun, J. B.
    Pan, L. W.
    Hu, Z. L.
    KOVOVE MATERIALY-METALLIC MATERIALS, 2020, 58 (06): : 395 - 407
  • [4] Processing and characterization of syntactic carbon foams containing hollow carbon microspheres
    Zhang, Liying
    Ma, J.
    CARBON, 2009, 47 (06) : 1451 - 1456
  • [5] Stereolithography fabrication and characterization of syntactic foams containing hollow glass microspheres
    Roques-Carmes, T.
    Marchal, Ph
    Gigante, A.
    Corbel, S.
    RUSSIAN CHEMICAL REVIEWS, 2009, 78 (04) : 375 - 386
  • [6] Compressive Characterization of Single Porous SiC Hollow Particles
    Vasanth Chakravarthy Shunmugasamy
    Steven E. Zeltmann
    Nikhil Gupta
    Oliver M. Strbik
    JOM, 2014, 66 : 892 - 897
  • [7] Compressive Characterization of Single Porous SiC Hollow Particles
    Shunmugasamy, Vasanth Chakravarthy
    Zeltmann, Steven E.
    Gupta, Nikhil
    Strbik, Oliver M., III
    JOM, 2014, 66 (06) : 892 - 897
  • [8] Dynamic Attenuation and Compressive Characterization of Syntactic Foams
    Ale, Bhaskar
    Rousseau, Carl-Ernst
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 2013, 135 (03):
  • [9] Compressive Properties of Poly (Dimethylsiloxane)-Hollow Glass Microballoons Syntactic Foams
    Upadhyay, Alok
    Ullas, A., V
    CELLULAR POLYMERS, 2022, 41 (06) : 243 - 251
  • [10] Compressive properties of the magnesium matrix syntactic foams using different types of porous volcanic rock particles
    Dong, Zhiqiang
    Song, Da
    Sun, Weibo
    Wang, Jin
    Liu, Jiaan
    MATERIALIA, 2022, 25
12345