High-temperature tensile properties of laser powder bed fusion Ti-6.5Al-2Zr-1Mo-1V alloy after annealing

被引：1

作者：

Zhou, Jiachen ^{[1
,2
]}

Su, Baoxian ^{[1
,2
,3
]}

Zhu, Guoqiang ^{[1
,2
]}

Jin, Yinling ^{[4
]}

Wang, Binbin ^{[1
,2
]}

Luo, Liangshun ^{[1
,2
]}

Chen, Ruirun ^{[1
]}

Wang, Liang ^{[1
,2
]}

Yang, Qian ^{[5
]}

Yu, Yongsheng ^{[3
]}

Su, Yanqing ^{[1
,2
]}

机构：

[1] Harbin Inst Technol, Sch Mat Sci & Engn, Natl Key Lab Precis Hot Proc Met, Harbin 150001, Peoples R China

[2] Harbin Inst Technol, Zhengzhou Res Inst, Zhengzhou 450000, Peoples R China

[3] Harbin Inst Technol, Sch Chem & Chem Engn, State Key Lab Urban Water Resource & Environm, Harbin 150001, Peoples R China

[4] Shenyang Aircraft Corp, Shenyang 110850, Peoples R China

[5] Yunnan Natl Titanium Met Co Ltd, Chuxiong 651200, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2025年 / 923卷

基金：

中国博士后科学基金; 中国国家自然科学基金;

关键词：

TA15; alloy; Laser powder bed fusion; Microstructure; High-temperature tensile property; MELTED TI-6AL-4V ALLOY; TA15; TITANIUM-ALLOY; MECHANICAL-PROPERTIES; DEFORMATION-BEHAVIOR; MICROSTRUCTURE; EVOLUTION; SLIP; DECOMPOSITION; DUCTILITY; STRESS;

D O I：

10.1016/j.msea.2024.147700

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Herein, the high-temperature tensile deformation behavior in the range of 500-750 degrees C for laser powder bed fusion (L-PBF) Ti-6.5Al-2Zr-1Mo-1V (TA15) alloy after annealing treatment has been investigated in detail. The experimental results show that the ultimate tensile strength (UTS) and yield strength (YS) of the sample decrease gradually with the increase of test temperature, while the elongation (EL) of the sample increases gradually. The reduction in strength can be attributed to the decrease in dislocation density. When the tensile temperature is below 550 degrees C, a pronounced work-hardening phenomenon can be observed. At temperatures above 650 degrees C, significant dynamic recovery and dynamic recrystallization effects lead to significant softening. When the tensile temperature is below 600 degrees C, the fracture mode is transgranular fracture, while when the temperature is 650 degrees C, the fracture mode changes to intergranular fracture. After annealing, L-PBF TA15 samples exhibit excellent mechanical properties at medium to high temperatures, which provides an important reference value for the application of L-PBF fabricated titanium alloy components in the aerospace industries.

引用

页数：12

共 51 条

[51] Deciphering the microstructural development and excellent ductility in electron beam wire-fed additive manufacturing of Ti-6Al-3Nb-2Zr-1Mo alloys based on high deposition rate [J].

Zhu, Guoqiang ;

Wang, Liang ;

Su, Baoxian ;

Wang, Binbin ;

Cui, Ran ;

Yan, Hui ;

Jiang, Botao ;

Zhou, Jiachen ;

Chen, Ruirun ;

Luo, Liangshun ;

Su, Yanqing ;

Guo, Jingjie .

ADDITIVE MANUFACTURING, 2024, 94