Effect of Si:C ratio on porosity and flexural strength of porous self-bonded silicon carbide ceramics

被引：0

作者：

Department of Materials Science and Engineering, University of Seoul, Seoul 130-743, Korea, Republic of ^{[1
]}

不详 ^{[2
]}

机构：

[1] Department of Materials Science and Engineering, University of Seoul

[2] Energy Materials Research Center, Korea Institute of Energy Research

来源：

J. Korean Ceram. Soc. | 2008年 / 5卷 / 285-289期

关键词：

Porosity; Porous ceramics; Self-bonded SiC; Silicon carbide; Strength;

D O I：

10.4191/KCERS.2008.45.5.285

中图分类号：

学科分类号：

摘要：

Porous self-bonded silicon carbide (SiC) ceramics were fabricated at temperatures ranging from 1750 to 1850°C using SiC, silicon (Si), and carbon (C) powders as starting materials. The effect of the Si:C ratio on porosity and strength was investigated as a function of sintering temperature. It was possible to produce self-bonded SiC ceramics with porosities ranging from 36% to 43%. The porous ceramics showed a maximal porosity when the Si:C ratio was 2:1 regardless of the sintering temperature. In contrast, the maximum strength was obtained when the ratio was 5:1.

引用

页码：285 / 289

页数：4

共 50 条

[31] Corrosion behaviors of porous reaction-bonded silicon carbide ceramics incorporated with CaO [J].

Han, Feng ;

Xu, Chaonan ;

Wei, Wei ;

Zhang, Feng ;

Xu, Peng ;

Zhong, Zhaoxiang ;

Xing, Weihong .

CERAMICS INTERNATIONAL, 2018, 44 (11) :12225-12232

[32] Effect of Starting SiC Particle Size on Nitridation and Strength of Silicon Nitride-Bonded Silicon Carbide Ceramics [J].

Choi, Young-Hoon ;

Kim, Young-Wook ;

Woo, Sang-Kuk ;

Han, In-Sub .

JOURNAL OF THE KOREAN CERAMIC SOCIETY, 2010, 47 (02) :157-162

[33] A statistical approach to strength evaluation incorporating porosity effect for porous ceramics [J].

Hoshide, T ;

Abe, J .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2003, 26 (05) :383-389

[34] Investigation of flexural strength and porosity of porous Si3N4 ceramics through orthogonal experimental design [J].

Yu, Juanli ;

Wang, Hongjie ;

Hou, Jianmei ;

Zhang, Jian ;

Qiao, Guanjun ;

Jin, Zhihao .

JOURNAL OF CERAMIC PROCESSING RESEARCH, 2008, 9 (06) :624-629

[35] Thermal shock resistance of in situ reaction bonded porous silicon carbide ceramics [J].

Ding, Shuqiang ;

Zeng, Yu-Ping ;

Jiang, Dongliang .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 425 (1-2) :326-329

[36] Effect of particle dispersion on microstructure and strength of reaction-bonded silicon carbide [J].

Paik, U ;

Park, HC ;

Choi, SC ;

Ha, CG ;

Kim, JW ;

Jung, YG .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 334 (1-2) :267-274

[37] Gas permeability and adsorbability of the glass-bonded porous silicon carbide ceramics with controlled pore size [J].

Wang, Bo ;

Zhang, Hui ;

Phuong, Hoang-Tuan ;

Jin, Feng ;

Yang, Jian-Feng ;

Ishizaki, Kozo .

CERAMICS INTERNATIONAL, 2015, 41 (02) :2279-2285

[38] Tailoring porosity and pore size in silicon carbide ceramics with C/SiO2 additions [J].

Yin, Kexin ;

Sun, Wenyue ;

Yi, Menghuan ;

Hu, Pu ;

Huang, Zhiliang ;

Chen, Changlian .

INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2025, 22 (03)

[39] Improvement in fracture strength of porous reaction-bonded silicon carbide with unique surface layer by incorporating α-silicon carbide powder as a secondary phase [J].

Shimamura, Akihiro ;

Katsui, Hirokazu ;

Zhou, You ;

Hotta, Mikinori ;

Kondo, Naoki ;

Fukushima, Manabu .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2022, 42 (13) :5458-5463

[40] Fabrication of mullite-bonded porous silicon carbide ceramics by in situ reaction bonding [J].

Ding, Shuqiang ;

Zhu, Sumin ;

Zeng, Yu-Ping ;

Jiang, Dongliang .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (04) :2095-2102

← 1 2 3 4 5 →