Effect of Si:C ratio on porosity and flexural strength of porous self-bonded silicon carbide ceramics

被引：0

作者：

Department of Materials Science and Engineering, University of Seoul, Seoul 130-743, Korea, Republic of ^{[1
]}

不详 ^{[2
]}

机构：

[1] Department of Materials Science and Engineering, University of Seoul

[2] Energy Materials Research Center, Korea Institute of Energy Research

来源：

J. Korean Ceram. Soc. | 2008年 / 5卷 / 285-289期

关键词：

Porosity; Porous ceramics; Self-bonded SiC; Silicon carbide; Strength;

D O I：

10.4191/KCERS.2008.45.5.285

中图分类号：

学科分类号：

摘要：

Porous self-bonded silicon carbide (SiC) ceramics were fabricated at temperatures ranging from 1750 to 1850°C using SiC, silicon (Si), and carbon (C) powders as starting materials. The effect of the Si:C ratio on porosity and strength was investigated as a function of sintering temperature. It was possible to produce self-bonded SiC ceramics with porosities ranging from 36% to 43%. The porous ceramics showed a maximal porosity when the Si:C ratio was 2:1 regardless of the sintering temperature. In contrast, the maximum strength was obtained when the ratio was 5:1.

引用

页码：285 / 289

页数：4

共 50 条

[21] Effect of alkaline earth additives on the flexural strength of silicon oxycarbide-bonded silicon carbide ceramics [J].

Eom, Jung-Hye ;

Kim, Young-Wook ;

Jung, Byung Jun .

CERAMICS INTERNATIONAL, 2013, 39 (02) :2083-2091

[22] Effect of Template Size Ratio on Porosity and Strength of Porous Zirconia Ceramics [J].

Chae, Su-Ho ;

Kim, Young-Wook ;

Song, In-Hyuck ;

Kim, Hai-Doo ;

Bae, Ji Soo .

JOURNAL OF THE KOREAN CERAMIC SOCIETY, 2008, 45 (09) :537-543

[23] Effect of forming methods on porosity and compressive strength of polysiloxane-derived porous silicon carbide ceramics [J].

Eom, Jung-Hye ;

Kim, Young-Wook ;

Park, Chul B. ;

Wang, Chunmin .

JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2012, 120 (1401) :199-203

[24] Preparation and characterization of cordierite-bonded silicon carbide porous ceramics [J].

Lee, Jin-Seok ;

Choi, Do-Mun ;

Choi, Sung-Churl .

ADVANCES IN NANOMATERIALS AND PROCESSING, PTS 1 AND 2, 2007, 124-126 :747-+

[25] Effect of initial α-phase content on microstructure and flexural strength of macroporous silicon carbide ceramics [J].

Jung-Hye Eom ;

Young-Wook Kim .

Metals and Materials International, 2012, 18 :379-383

[26] Effect of initial α-phase content on microstructure and flexural strength of macroporous silicon carbide ceramics [J].

Eom, Jung-Hye ;

Kim, Young-Wook .

METALS AND MATERIALS INTERNATIONAL, 2012, 18 (02) :379-383

[27] Processing and mechanical properties of porous silica-bonded silicon carbide ceramics [J].

Chun, YS ;

Kim, YW .

METALS AND MATERIALS INTERNATIONAL, 2005, 11 (05) :351-355

[28] Processing and mechanical properties of porous silica-bonded silicon carbide ceramics [J].

Yong-Seong Chun ;

Young-Wook Kim .

Metals and Materials International, 2005, 11 :351-355

[29] Microstructure and strength of oxidation-bonded porous silicon nitride ceramics [J].

Ding, Shuqiang ;

Zeng, Yuping ;

Jiang, Dongliang .

PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 :503-506

[30] Effect of recoating slurry viscosity on the properties of reticulated porous silicon carbide ceramics [J].

Yao, XM ;

Tan, SH ;

Huang, ZR ;

Jiang, DL .

CERAMICS INTERNATIONAL, 2006, 32 (02) :137-142

← 1 2 3 4 5 →