Insights into dissolved oxygen dependent crack initiation mechanism of 316LN stainless steel fatigue tested in high-temperature pressurized water

被引：0
|
作者：
Qiao, Yufei [1 ,2 ]
Li, Hui [3 ]
Tan, Jibo [1 ]
Liu, Daoping [3 ]
Zhang, Ziyu [1 ]
Wu, Xinqiang [1 ]
Ke, Wei [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
[3] Nucl Power Inst China, Sci & Technol Reactor Syst Design Technol Lab, Chengdu 610041, Peoples R China
来源：
CORROSION SCIENCE | 2025年 / 244卷
基金：
中国国家自然科学基金;
关键词：
Stainless steel; Dissolved oxygen; Corrosion fatigue; TEM; High temperature corrosion; LOW-CYCLE FATIGUE; ENVIRONMENTALLY ASSISTED CRACKING; CORROSION-FATIGUE; ALLOY; 690; GROWTH-BEHAVIOR; CHEMISTRY; CARBON;
D O I：
10.1016/j.corsci.2024.112662
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion fatigue behavior of 316LN SS hollow specimen was investigated in high-temperature pressurized water at different dissolved oxygen (DO) concentrations (<5-200 ppb). The fatigue life of 316LN SS significantly increased with increasing DO concentration from < 5-20 ppb, while the effect of DO on fatigue lives apparently saturated at above 20 ppb (20-200 ppb). DO plays a significant role in microstructurally small cracks rather than mechanically small cracks. The oxidation characteristic of slip bands affects the crack initiation process. The effect of DO on the fatigue crack initiation mechanism is discussed.
引用
收藏
页数：19
相关论文
共 50 条
  • [41] Effect of temperature, chloride and dissolved oxygen concentration on the open circuit and transpassive potential values of 316L stainless steel at high-temperature pressurized water
    Arjmand, Farzin
    Zhang, Lefu
    Wang, Jiamei
    NUCLEAR ENGINEERING AND DESIGN, 2017, 322 : 215 - 226
  • [42] Crack initiation mechanisms for low cycle fatigue of type 316Ti stainless steel in high temperature water
    Xu, S.
    Wu, X. Q.
    Han, E. H.
    Ke, W.
    Katada, Y.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 490 (1-2): : 16 - 25
  • [43] Effects of surface nanocrystallization on the oxide film formed on 316LN stainless steel in a high-temperature aqueous environment
    Chen, Xudong
    Dai, Xin
    Qian, Hongchang
    Yang, Bin
    Zhao, Jiqing
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (01): : 125 - 133
  • [44] Effect of laser shock peening on high cycle fatigue characteristics of 316LN stainless steel
    Yella, Pardhu
    Rajulapati, K., V
    Reddy, G. V. Prasad
    Sandhya, R.
    Kiran, P. Prem
    Buddu, Ramesh K.
    Rao, K. Bhanu Sankara
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2019, 176
  • [45] Effects of Forging and Heat Treatments on the Microstructure and Oxidation Behavior of 316LN Stainless Steel in High Temperature Water
    Yueling Guo
    En-Hou Han
    Jianqiu Wang
    Journal of Materials Science & Technology, 2015, 31 (04) : 403 - 412
  • [46] Stress Corrosion Cracking of Nitrogen-containing Stainless Steel 316LN in High Temperature Water Environments
    YANG Wu1
    Chinese Journal of Mechanical Engineering, 2010, 23 (06) : 677 - 683
  • [47] Microcrack initiation mechanisms of 316LN austenitic stainless steel under in-phase thermomechanical fatigue loading
    Li, Bingbing
    Zheng, Yiming
    Shi, Shouwen
    Liu, Yanming
    Li, Yajing
    Chen, Xu
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 752 : 1 - 14
  • [48] Effects of Forging and Heat Treatments on the Microstructure and Oxidation Behavior of 316LN Stainless Steel in High Temperature Water
    Guo, Yueling
    Han, En-Hou
    Wang, Jianqiu
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2015, 31 (04) : 403 - 412
  • [49] Stress Corrosion Cracking of Nitrogen-containing Stainless Steel 316LN in High Temperature Water Environments
    Yang Wu
    Li Guangfu
    Huang Chunbo
    Zhou Jianjiang
    Lue Zhanpeng
    CHINESE JOURNAL OF MECHANICAL ENGINEERING, 2010, 23 (06) : 677 - 683
  • [50] Evaluation of the creep-fatigue damage mechanism of Type 316L and Type 316LN stainless steel
    Kim, Dae Whan
    Chang, Jong-Hwa
    Ryu, Woo-Seog
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2008, 85 (06) : 378 - 384
12345