Damage mechanism of railway wheels under condition with angle of attack

被引：0

作者：

Zhou, Gui-Yuan ^{[1
]}

He, Cheng-Gang ^{[1
]}

Liu, Ji-Hua ^{[1
]}

Liu, Qi-Yue ^{[1
]}

机构：

[1] Tribology Research Institute, School of Mechanical Engineering, Southwest Jiaotong University, Chengdu

来源：

Mocaxue Xuebao/Tribology | 2015年 / 35卷 / 06期

基金：

中国国家自然科学基金;

关键词：

Angle of attack; Fatigue crack; Plastic accumulation; Railway wheels;

D O I：

10.16078/j.tribology.2015.06.017

中图分类号：

学科分类号：

摘要：

There will generate an angle of attack between railway wheels and rails under curve negotiating and hunting conditions. With the aim of investigating the damage mechanisms of railway wheels under condition with angle of attack, the rolling contact fatigue test of simulate wheel was performed using a JD-1 wheel/rail simulation facility. The results indicate that different damage mechanism occurred at the different region of wheel specimen, and the regions were divided into three parts, i.e. the plastic accumulation region, the fatigue region and the worn region. Drastic changing in stress and the stress direction was from the high stress region to the lower one, it world appear the material accumulation which led to fatigue crack initiation. Rolling contact fatigue cracks initiated at surface or sub-surface in the fatigue region, and the grains of wheel material became elongated obviously under high stress, showing fibrous shape in cross section. © 2015, Science Press. All right reserved.

引用

页码：768 / 773

页数：5

共 18 条

[1]

Ekberg A., Akesson B., Kabo E., Wheel/rail rolling contact fatigue - Probe, predict, prevent, Wear, 314, 1-2, pp. 2-12, (2014)

[2]

Handa K., Morimoto F., Influence of wheel/rail tangential traction force on thermal cracking of railway wheels, Wear, 289, pp. 112-118, (2012)

[3]

Johnson K.L., The strength of surfaces in rolling contact, Proceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science, 203, pp. 151-163, (1989)

[4]

Tong J., Zhao L.G., Lin B., Ratchetting strain as a driving force for fatigue crack growth, International Journal of Fatigue, 46, pp. 49-57, (2013)

[5]

Langueh A., Brunel J.F., Charkaluk E., Et al., Influence of the steel grades on rolling contact fatigue of railway wheels, Procedia Engineering, 10, pp. 2627-2632, (2011)

[6]

Bevan A., Molyneux-Berry P., Eickhoff B., Et al., Development and validation of a wheel wear and rolling contact fatigue damage model, Wear, 307, 1-2, pp. 100-111, (2013)

[7]

Jin X.S., Liu Q.Y., Tribology of Wheel and Rail, (2004)

[8]

Donzella G., Faccoli M., Mazzu A., Et al., Progressive damage assessment in the near-surface layer of railway wheel-rail couple under cyclic contact, Wear, 271, 1-2, pp. 408-416, (2011)

[9]

Dirks B., Enblom R., Prediction model for wheel profile wear and rolling contact fatigue, Wear, 271, 1-2, pp. 210-217, (2011)

[10]

Sandstrom J., Subsurface rolling contact fatigue damage of railway wheels - A probabilistic analysis, International Journal of Fatigue, 37, pp. 146-152, (2012)

← 1 2 →