Effect of solution temperature on microstructure and pitting corrosion resistance of S32760 duplex stainless steel

被引：0
作者：
Chen, Yulai [1 ]
Luo, Zhaoyin [2 ]
Li, Jingyuan [2 ]
机构：
[1] Metallurgical Engineering Research Institute, University of Science and Technology Beijing, Beijing
[2] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing
来源：
Jinshu Xuebao/Acta Metallurgica Sinica | 2015年 / 51卷 / 09期
基金：
中国国家自然科学基金;
关键词：
Corrosion resistance; Duplex stainless steel; Precipitation; Solution treatment;
D O I：
10.11900/0412.1961.2015.00044
中图分类号：
学科分类号：
摘要：
In order to obtain the optimal corrosion resistance, the characteristics of microstructure and alloy elements distribution of S32760 duplex stainless steel were studied after solid solution treatment at various temperatures from 1000 ℃ to 1300 ℃ by means of OM, EPMA, SEM, EDS and TEM. In addition, the pitting corrosion resistance was measured by the electrochemical workstation. The results show that the N atoms diffused into δ phase from γ phase during solution treatment when the temperature was higher than 1080 ℃. N atoms migrated back into γ phase when the subsequent cooling was slow enough. However, Cr2N phase in situ precipitated during quenching because there was not enough time for the N atoms to diffuse back into γ phase. Cr2N particles increased with the solution temperature increasing. Furthermore, σ phase precipitated when the tested sheet was heat treated at or below 1040 ℃ due to the high content of N. Thus it is obvious that the solution temperature range of the S32750 duplex stainless steel is quite narrow, which is between 1040 ℃ and 1080 ℃, and it is confirmed that the optimal temperature is 1060 ℃. After treated at 1060 ℃ for 60 min, the Brinell hardness of S32760 steel is 249 HBW, pitting potential is up to 1068 mV and the passive current density is as low as 1.48×10-4 A/cm2. © All right reserved.
引用
收藏
页码：1085 / 1091
页数：6
相关论文
共 25 条
  • [1] Gurrappa I., Krishna Reddy C.V., J Mater Process Technol, 182, (2007)
  • [2] Huang C.S., Shih C.C., Mater Sci Eng, A402, (2005)
  • [3] Migiakis K., Daniolos N., Papadimitriou G.D., Mater Manuf Processes, 25, (2010)
  • [4] Sun X.G., Shanxi Metall, 3, (2013)
  • [5] Wu J., Duplex Stainless Steel, (1999)
  • [6] Yang S.M., Chen Y.C., Chen C.H., Huang W.P., Lin D.Y., J Alloys Compd, 633, (2015)
  • [7] Fargas G., Anglada M., Mateo A., J Mater Process Technol, 209, (2009)
  • [8] Bettini E., Kivisakk U., Leygraf C., Pan J., Electrochim Acta, 113, (2013)
  • [9] Du J., Wang C., Wang K., Chen K., Intermetallics, 45, (2014)
  • [10] Chen X.H., Ren X.P., Xu H., Tong J.G., Zhang H.Y., Int J Min Met Mater, 19, (2012)
123