Synthesis and characterisation of amorphous SeTe nanorods prepared by ball milling

被引：2

作者：

Al-Ghamdi, A.A. ^{[1
]}

Faidah, Adel S. ^{[1
]}

Yaghmour, S.J. ^{[1
]}

Al-Heniti, S. ^{[1
]}

Al-Hazmi, F.S. ^{[1
]}

Khan, Shamshad A. ^{[1
,2
]}

机构：

[1] Department of Physics, Faculty of Science, King Abdul Aziz University

[2] Department of Physics, St. Andrew's P.G. College

来源：

International Journal of Nanomanufacturing | 2009年 / 4卷 / 1-4期

关键词：

Amorphous materials; Amorphous nanoparticles; Ball milling; Nanorods; Optical band gap mechanical alloying; X-ray diffraction; XRD;

D O I：

10.1504/IJNM.2009.028126

中图分类号：

学科分类号：

摘要：

The amorphous Se97Te3 nanorods were prepared by mechanical milling. The amorphous Se97Te3 materials were used as a starting material. The milled materials were characterisation by XRD, TEM and optical measurement by JASCO, UV/VIS/ NIR spectrophotometer in a wavelength region 300 nm-1000 nm. The experimental result shows that an amorphous stage is also achieved during the milling process. TEM analysis showed that after 50 hours of milling time, multi-walled amorphous nanorods were formed with a diameter of about 90 nm and after 60 hours of milling time amorphous nanowires of about 80 nm diameter was formed. The optical absorption measurement indicates that the absorption mechanism is due to indirect transition. It has been observed that the absorption coefficient increases lineally with the increase in photon energy and the optical band gap increases with the increase of milling time. Copyright © 2009, Inderscience Publishers.

引用

页码：197 / 207

页数：10

共 20 条

[1]

Ahmad A., Khan S.A., Sinha K., Kumar L., Khan Z.H., Zulfequar M., Husain M., Optical characterization of vacuum evaporated a-Se80Te20-xCux thin films, Vacuum, 82, 6, pp. 608-612, (2008)

[2]

Gan K., Gu M., The compressibility of Cu/SiCp powder prepared by high-energy ball milling, J. Materials Proc. Tech, 199, pp. 173-177, (2008)

[3]

Gao X., Gao T., Zhang L., Solution-solid growth of α-monoclinic selenium nanowires at room temperature, Journal of Materials Chemistry, 13, pp. 6-8, (2003)

[4]

Guittoum A., Layadi A., Bourzami A., Tafat H., Souami N., Boutarfaia S., Lacour D., X-ray diffraction, microstructure, Mössbauer and magnetization studies of nanostructured Fe50Ni50 alloy prepared by mechanical alloying, J. Magnetism and Magnetic Materials, 320, pp. 1385-1392, (2008)

[5]

Husain M., Khan Z.H., Zulfequar M., Sharma T.P., Optical properties of a-Ga20Se80-xSbx thin films, Optical Materials, 6, 3, pp. 139-146, (1996)

[6]

Ilyas M., Zulfequar M., Khan Z.H., Husain M., Optical band gap and optical constants in a-GaxTe100-x thin films, Optical Materials, 11, 1, pp. 67-77, (1998)

[7]

Khan S.A., Zulfequar M., Husain M., Optical band gap and optical constants in a-Se80Te20-xPbx thin films, Current Applied Physics, 5, 6, pp. 583-587, (2005)

[8]

Lee H.S., Cheong B., Lee T.S., Lee K.S., Kim W.M., Huh J.Y., A semiconducting thermooptic material for potential application to super-resolution optical data storage', i, Surface & Coatings Technology, 193, pp. 335-339, (2005)

[9]

Majeed Khan M.A., Zulfequar M., Husain M., Optical investigation of a-Se100-xBix alloys, Optical Materials, 22, 1, pp. 21-29, (2003)

[10]

Molina Concha B., De Biasi E., Zysler R.D., Monte Carlo simulation of Fe-Co amorphous nanoparticles magnetization, Physica B, 403, pp. 390-393, (2008)

← 1 2 →