Parameter sensitivity analysis of Al2O3-13%TiO2 composite ceramic coating thickness by electro-brush plating

被引：0
|
作者：
Shi, Li-Ping [1 ]
Wu, Yu-Guo [1 ]
Zhang, Jin-Chao [1 ]
Zhang, Hu-Dong [2 ]
机构：
[1] School of Mechanical Engineering, Anhui University of Technology, Ma'anshan 243032, China
[2] Ma'anshan Kaimin Wire Rope Limited Liability Company, Ma'anshan 243000, China
来源：
Fenmo Yejin Cailiao Kexue yu Gongcheng/Materials Science and Engineering of Powder Metallurgy | 2012年 / 17卷 / 06期
关键词：
Aluminum oxide - Titanium dioxide - Alumina - Ceramic materials - Thickness measurement - Ceramic coatings - Plating;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
For Al2O3-13%TiO2 (AT13) composite ceramic coating fabricated by electro-brush plating, the process parameters affecting coating thickness were evaluated and the sensitive factor was identified through the multi-parameter sensitivity analysis method. By central composite design experiment, the sensitivity function was established, the process parameters affecting coating thickness were analyzed and the result of sensitivity analysis was compared to the result of variance analysis. It is shown that plating head speed (SV*=4.3528) is the main parameter, followed by current (SI*=0.2893) and voltage (SU*=0.2492), and the result of sensitivity analysis is consistent with the analysis of variance; the method can be used to optimize the process parameters of composite ceramic coating by electro-brush plating.
引用
收藏
页码：700 / 705
相关论文
共 50 条
  • [31] Microstructure characteristics of Al2O3-13 wt.% TiO2 coating plasma spray deposited with nanocrystalline powders
    Zhang, Jianxin
    He, Jining
    Dong, Yanchun
    Li, Xiangzhi
    Yan, Dianran
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 197 (1-3) : 31 - 35
  • [32] Laser remelting of plasma sprayed Al2O3+13wt%TiO2 ceramic coating
    Yang, Yuanzheng
    Liu, Zhiguo
    Liu, Zhengyi
    Zhuang, Yuzhi
    Jiguang Zazhi/Laser Journal, 2000, 21 (01): : 46 - 47
  • [33] Structure and wear resistance of plasma sprayed Al2O3+13%TiO2 ceramic coating
    Yang, Yuanzheng
    Liu, Zhengyi
    Zhuang, Yuzhi
    Gongneng Cailiao/Journal of Functional Materials, 2000, 31 (04): : 390 - 392
  • [34] Effects of Al2O3-13% TiO2 Coating Particle Size on Commercial Mild Steel via Plasma Spray Method
    Hassanuddin, N.
    Ghazali, M. J.
    Muchtar, A.
    Isa, M. C.
    Daud, A. R.
    FRACTURE AND STRENGTH OF SOLIDS VII, PTS 1 AND 2, 2011, 462-463 : 645 - +
  • [35] Effects of n-Al2O3 Particles Content on Structure and Performance of Electro-Brush Plating Ni-Co Alloy Composite Coatings
    Wang Xiaohe
    Lu Biao
    Hu Zhenfeng
    Xu Binshi
    RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (01) : 36 - 41
  • [36] Microstructure and properties of Al2O3-13%TiO2 coatings sprayed using nanostructured powders
    ZHANG Jianxin
    RareMetals, 2007, (04) : 391 - 397
  • [37] Nlicrostructure and properties of Al2O3-13%TiO2 coatings sprayed using nanostructured powders
    Zhang Jianxin
    He Jining
    Dong Yanchun
    Li Xiangzhi
    Yan Dianran
    RARE METALS, 2007, 26 (04) : 391 - 397
  • [38] Effects of n-Al2O3 particles content on structure and performance of electro-brush plating Ni-Co alloy composite coatings
    Wang, Xiaohe
    Lü, Biao
    Hu, Zhenfeng
    Xu, Binshi
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2016, 45 (01): : 36 - 41
  • [39] Microstructure evolution of laser remelted Al2O3-13 wt.%TiO2 coatings
    Li, C. G.
    Yu, Z. S.
    Zhang, Y. F.
    Zhang, P. L.
    Yan, H.
    Lu, Q. H.
    Li, W. G.
    Wang, Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 576 : 187 - 194
  • [40] Protection Performance of Plasma Sprayed Al2O3-13 wt%TiO2 Coating Sealed with an Organic-inorganic Hybrid Agent
    张凯城
    周泽华
    DENG Yong
    WANG Guangyu
    WANG Zehua
    WU Lintao
    YANG Guangheng
    Journal of Wuhan University of Technology(Materials Science), 2022, 37 (03) : 331 - 335
12345