The effect of nano-sized precipitates on stress corrosion cracking propagation of Alloy 718 under constant loads in PWR primary water

被引：0
|
作者：
Wang, Jiamei [1 ]
Zhu, Tianyu [1 ]
Wu, Yule [1 ]
Chen, Kai [1 ]
Guo, Xianglong [1 ]
Ren, Quanyao [2 ]
Li, Yuanming [2 ]
Tang, Chuanbao [2 ]
Yi, Hongpu [2 ]
Ye, Liang [4 ]
Xu, Shihao [4 ]
Zhang, Jing [3 ]
Tian, Wenxi [3 ]
Zhang, Lefu [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Nucl Sci & Engn, Shanghai 200240, Peoples R China
[2] Nucl Power Inst China, Sci & Technol Reactor Syst Design Technol Lab, Chengdu 610213, Peoples R China
[3] Xi An Jiao Tong Univ, Sch Energy & Power Engn, Xian 710049, Peoples R China
[4] China Nucl Power Technol Res Inst Co Lto, Shenzhen 518000, Peoples R China
来源：
CORROSION SCIENCE | 2025年 / 242卷
关键词：
Alloy; 718; Precipitates; Stress corrosion cracking; Crack growth rate; TEM; TKD; STAINLESS-STEEL; HYDROGEN EMBRITTLEMENT; HEAT-TREATMENT; NICKEL-ALLOYS; GROWTH RATE; TEMPERATURE; SCC; BEHAVIOR; MICROSTRUCTURE; PREDICTION;
D O I：
10.1016/j.corsci.2024.112577
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The stress corrosion cracking (SCC) propagation behavior of solution-annealed and precipitation-hardened Alloy 718 was investigated. The results show gamma '' and gamma ' precipitates are beneficial on retarding its crack growth under constant loads. Nano-sized precipitates at grain boundary (GB) tend to impede GB migration and oxidation beyond the crack tip, thereby compensating for the detrimental effect of a steeper strain gradient resulting from prominent elevated yield strength. The observed 2-40 times increase in CGR in hydrogenated water (near the Ni/ NiO boundary) primarily attributes to the preferential GB oxidation and instability of the oxides during phase transition.
引用
收藏
页数：15
相关论文
共 50 条
  • [1] Effect of material chemical composition on oxidation and stress corrosion cracking of the submerged arc welding Alloy 52M overlay in a simulated PWR primary water
    Xu, Xinhe
    Jia, Yibo
    Pan, Deng
    Cui, Tongming
    Lu, Zhanpeng
    Lozano-Perez, Sergio
    Chen, Junjie
    Li, Shuangyan
    Shoji, Tetsuo
    JOURNAL OF NUCLEAR MATERIALS, 2024, 588
  • [2] A review of stress corrosion cracking of austenitic stainless steels in PWR primary water
    Ehrnsten, Ulla
    Andresen, Peter L.
    Que, Zaiqing
    JOURNAL OF NUCLEAR MATERIALS, 2024, 588
  • [3] Assessing the influence of welding-induced mechanics on oxidation and stress corrosion cracking in an Alloy 600-Alloy 152 M weldment under simulated PWR primary water
    Xu, Xinhe
    Pan, Deng
    Li, Entong
    Lu, Zhanpeng
    Cui, Tongming
    Chen, Junjie
    Zheng, Hui
    Li, Kai
    Lozano-Perez, Sergio
    Shoji, Tetsuo
    JOURNAL OF NUCLEAR MATERIALS, 2024, 601
  • [4] The roles of thermal mechanical treatment and δ phase in the stress corrosion cracking of alloy 718 in primary water
    Wang, M.
    Song, M.
    Was, G. S.
    Nelson, J. L.
    CORROSION SCIENCE, 2019, 160
  • [5] The effect of cold rolling on grain boundary structure and stress corrosion cracking susceptibility of twins in alloy 690 in simulated PWR primary water environment
    Kuang, Wenjun
    Was, Gary S.
    Miller, Cody
    Kaufman, Mike
    Alam, Talukder
    Gwalani, Bharat
    Banerjee, Rajarshi
    CORROSION SCIENCE, 2018, 130 : 126 - 137
  • [6] STRESS CORROSION CRACKING OF NICKEL WELD METALS IN PWR PRIMARY WATER
    Xiong Ru
    Zhao Yuxiang
    Liu Guiliang
    PROCEEDINGS OF THE 21ST INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING - 2013, VOL 1, 2014,
  • [7] STRESS CORROSION CRACKING OF ALLOY 600 IN PWR PRIMARY WATER : INFLUENCE OF CHROMIUM, HYDROGEN AND OXYGEN DIFFUSION
    Guerre, C.
    Laghoutaris, P.
    Chene, J.
    Marchetti, L.
    Molins, R.
    Duhamel, C.
    Sennour, M.
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 1477 - 1488
  • [8] Effect of nano-sized precipitates on the fatigue property of a lamellar structured high entropy alloy
    Liu, Kaimiao
    Gwalani, Bharat
    Komarasamy, Mageshwari
    Shukla, Shivakant
    Wang, Tianhao
    Mishra, Rajiv S.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 760 : 225 - 230
  • [9] Insights into the stress corrosion cracking propagation behavior of Alloy 690 and 316 L stainless steel in KOH versus LiOH oxygenated water
    Wang, Jiamei
    Zhu, Tianyu
    Bao, Yichen
    Liu, Xiaoqiang
    Shi, Xiuqiang
    Guo, Xianglong
    Han, Zhongli
    Andresen, Peter L.
    Zhang, Lefu
    Chen, Kai
    CORROSION SCIENCE, 2023, 224
  • [10] Proton irradiation assisted localized corrosion and stress corrosion cracking in 304 nuclear grade stainless steel in simulated primary PWR water
    Deng, Ping
    Peng, Qunjia
    Han, En-Hou
    Ke, Wei
    Sun, Chen
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 65 : 61 - 71
12345