Formation and microstructural characterization of Ti/TiC surface composite layer by laser alloying treatment using graphite powder

被引：0

作者：

Yamaguchi, Takuto ^{[1
,2
]}

Hagino, Hideki ^{[1
,2
]}

Takemura, Mamoru ^{[1
,2
]}

Nakahira, Atsushi ^{[1
,2
]}

机构：

[1] Technology Research Institute of Osaka Prefecture, 2-7-1 Ayumino, Izumi

[2] Dept. Materials Science, Osaka Prefecture University, 1-1 Gakuen-cho, Naka-ku, Sakai

来源：

Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy | 2014年 / 61卷 / 10期

关键词：

Graphite powder; Laser alloying; Titanium; Titanium carbide;

D O I：

10.2497/jjspm.61.481

中图分类号：

学科分类号：

摘要：

Titanium and its alloys have various excellent properties, such as good corrosion resistance and high specific strength. However, they have not been applied to the sliding parts under sever wear condition due to their poor tribological properties. In this study, laser alloying using graphite powder was carried out to form Ti/TiC composite surface layer on commercial pure titanium substrate for improving wear resistance. The effects of graphite powder size and laser irradiation parameters on the microstructure of laser alloyed zone were mainly investigated. In the laser alloyed zone, dendritic primary TiC and fine particles of eutectic TiC were observed. In the condition of higher laser traverse speed and larger size of graphite powder, undissolved graphite particles were observed.

引用

页码：481 / 486

页数：5