Texture evolution induced by extrusion parameters and its effect on strengthening-toughening mechanisms of Al-Mg-Si-Cu-Mn alloys

被引:1
|
作者
Li, Yuyu [1 ,2 ]
Zhao, Guoqun [1 ,2 ]
Sun, Lu [1 ,2 ]
Zhang, Bo [3 ]
Zhao, Xingting [4 ]
机构
[1] Shandong Univ, State Key Lab Adv Equipment & Technol Met Forming, Jinan 250061, Shandong, Peoples R China
[2] Shandong Univ, Key Lab Liquid Solid Struct Evolut & Proc Mat, Minist Educ, Jinan 250061, Shandong, Peoples R China
[3] Shandong Weiqiao Pioneering Grp Co Ltd, Binzhou 256200, Peoples R China
[4] Linqu Inspect & Testing Ctr, Linqu 262600, Shandong, Peoples R China
关键词
Aluminum alloy; Extrusion; Microstructure; Texture; Mechanical properties; STRAIN-GRADIENT PLASTICITY; ALUMINUM-ALLOY; HOT EXTRUSION; GRAIN-BOUNDARY; MICROSTRUCTURE; DEFORMATION; TEMPERATURE;
D O I
10.1016/j.msea.2024.147377
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
In this study, extrusion experiments were carried out on Al-Mg-Si-Cu-Mn alloys with different extrusion ratios (ERs), extrusion temperatures (ETs), and extrusion speeds (ESs). By using electron backscatter diffraction (EBSD) analysis, tensile testing, and other analytical means, the evolution of microstructure, texture, and properties of the extruded alloys was systematically investigated, and the strengthening-toughening mechanism induced by the extrusion parameters was revealed. It was found that the strength of the extruded alloy shows a tendency to first increase and then decrease with the increase of the ER and ES, and the 'critical ER' and 'critical ES' are 29.5 and 2.5 mm/s, respectively; the strength of the extruded alloy gradually increases with the increase of the ET. The alloy achieved excellent strength-toughness matching at the ER of 29.5, ET of 480 degrees C, and ES of 2.5 mm/s. The yield strength (YS), ultimate tensile strength (UTS), and elongation (EL) of the extruded alloy at this condition were similar to 169.58 MPa, similar to 314.36 MPa, and similar to 16.57 %, respectively. This excellent strength-toughness matching is mainly related to the following aspects: 1) grain refinement provides high grain boundary strengthening effect and appropriate work hardening ability; 2) <111>//ED texture has a strong preferential orientation; 3) the variation trend of dislocation density is importantly related to <111>//ED and EXa{011}<111> textures; 4) Cube{001}<100> and Goss{011}<100> textures have a softening effect. The above findings provide new insights into the potential mechanisms of hot extrusion forming of aluminum alloys, which are of important guiding for the design and development of aluminum alloys with excellent strength-toughness combinations.
引用
收藏
页数:27
相关论文
共 50 条
  • [1] Research Progress on Microstructure Evolution and Strengthening-Toughening Mechanism of Mg Alloys by Extrusion
    Zheng, Yaqi
    Zhang, Yuan
    Liu, Yun
    Tian, Yaqiang
    Zheng, Xiaoping
    Chen, Liansheng
    MATERIALS, 2023, 16 (10)
  • [2] Precipitation behavior and strengthening-toughening mechanism of additive friction stir-deposited Al-Mg-Si-Cu alloy
    Tang, Wenshen
    Yang, Xinqi
    Luo, Ting
    Wang, Ruilin
    Gu, Chao
    ADDITIVE MANUFACTURING, 2023, 76
  • [3] Microstructures and strengthening mechanisms of high Fe containing Al–Mg–Si–Mn–Fe alloys with Mg, Si and Mn modified
    Wang, Yu
    Deng, Yunlai
    Dai, Qingsong
    Jiang, Keda
    Chen, Jiqiang
    Guo, Xiaobin
    Materials Science and Engineering: A, 2021, 803
  • [4] Microstructures and strengthening mechanisms of high Fe containing Al-Mg-Si-Mn-Fe alloys with Mg, Si and Mn modified
    Wang, Yu
    Deng, Yunlai
    Dai, Qingsong
    Jiang, Keda
    Chen, Jiqiang
    Guo, Xiaobin
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 803
  • [5] Improved Distribution and Uniformity of α-Al(Mn,Cr)Si Dispersoids in Al-Mg-Si-Cu-Mn (6xxx) Alloys by Two-Step Homogenization
    Li, Zhen
    Qin, Jian
    Zhang, Haitao
    Wang, Xiaoguo
    Zhang, Bo
    Nagaumi, Hiromi
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2021, 52 (08): : 3204 - 3220
  • [6] Bimodal grain structure formation and strengthening mechanisms in Mg-Mn-Al-Ca extrusion alloys
    Jianyue Zhang
    Peng Peng
    Qingshan Yang
    Alan A.Luo
    Journal of Magnesium and Alloys, 2023, (12) : 4407 - 4419
  • [7] Bimodal grain structure formation and strengthening mechanisms in Mg-Mn-Al-Ca extrusion alloys
    Zhang, Jianyue
    Peng, Peng
    Yang, Qingshan
    Luo, Alan A.
    JOURNAL OF MAGNESIUM AND ALLOYS, 2023, 11 (12) : 4407 - 4419
  • [8] Bimodal grain structure formation and strengthening mechanisms in Mg-Mn-Al-Ca extrusion alloys
    Jianyue Zhang
    Peng Peng
    Qingshan Yang
    Alan ALuo
    Journal of Magnesium and Alloys, 2023, 11 (12) : 4407 - 4419
  • [9] Improved Distribution and Uniformity of α-Al(Mn,Cr)Si Dispersoids in Al-Mg-Si-Cu-Mn (6xxx) Alloys by Two-Step Homogenization
    Zhen Li
    Jian Qin
    Haitao Zhang
    Xiaoguo Wang
    Bo Zhang
    Hiromi Nagaumi
    Metallurgical and Materials Transactions A, 2021, 52 : 3204 - 3220
  • [10] Microstructure Characteristics, Texture Evolution and Mechanical Properties of Al-Mg-Si-Mn-xCu Alloys via Extrusion and Heat Treatment
    Li, Zulai
    Zhang, Yingxing
    Zhang, Junlei
    Chen, Xiang
    Chen, Suokun
    Cui, Lujian
    Han, Shengjie
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2024, 37 (09) : 1501 - 1522