The roles of Ni segregation on the oxidation kinetics of austenitic stainless steel 316L exposed to oxygen-containing liquid lead-bismuth eutectic (LBE)

被引：0
|
作者：
Guo, Shaoqiang [1 ]
Chen, Jianye [1 ]
Ma, Zelin [1 ]
Du, Qian [1 ]
Lu, Chenyang [1 ]
Xie, Shijing [1 ]
Long, Bin [2 ]
Yun, Di [1 ]
Gu, Long [3 ]
机构：
[1] Xi An Jiao Tong Univ, Sch Nucl Sci & Technol, Shaanxi Key Lab Adv Nucl Energy & Technol, Xian 710049, Shaanxi, Peoples R China
[2] China Inst Atom Energy, POB 275-92, Beijing 102413, Peoples R China
[3] Lanzhou Univ, Sch Nucl Sci & Technol, Lanzhou 730000, Gansu, Peoples R China
来源：
CORROSION SCIENCE | 2025年 / 244卷
基金：
中国国家自然科学基金;
关键词：
A. Austenitic steel; B; TEM; EBSD; C. Liquid metal corrosion; C; Oxidation; FERRITIC-MARTENSITIC STEELS; LONG-TERM BEHAVIORS; FE-9CR-1MO STEEL; DEGREES-C; ELECTRON-MICROSCOPY; CORROSION BEHAVIOR; OXIDE SCALES; MECHANISM; TEMPERATURE; ALLOY;
D O I：
10.1016/j.corsci.2024.112644
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The micro-to-atomic structure of the oxide scale formed on AISI 316L austenitic stainless steel exposed to oxygen- containing liquid LBE at 550 degrees C is characterized by SEM-EDS, EBSD, FIB-TEM and synchrotron radiation microXRD. Nickel that was believed to be detrimental to steel corrosion in Pb-Bi is revealed to be beneficial on retarding the oxidation kinetics. Ni was not oxidized and existed as metallic Ni-rich nanophase in the internal oxidation zone (IOZ). The inward diffusion of Ni from IOZ to the bulk steel caused the segregation of coarse Nirich precipitates on grain boundaries and the steel/IOZ interface, which hindered the intergranular and possibly the trans-granular diffusion.
引用
收藏
页数：17
相关论文
共 50 条
  • [41] Corrosion Behavior of NbC and Its Effect on Corrosion Layer Formation in Liquid Lead-Bismuth Eutectic of Nb-Containing Austenitic Stainless Steel
    Wu, Yang
    Xie, Ang
    Chen, Shenghu
    Jiang, Haichang
    Rong, Lijian
    ACTA METALLURGICA SINICA, 2025, 61 (02)
  • [42] Thermochromatographic behavior of iodine in 316L stainless steel columns when evaporated from lead–bismuth eutectic
    Erik Karlsson
    Jörg Neuhausen
    Robert Eichler
    Ivan I. Danilov
    Alexander Vögele
    Andreas Türler
    Journal of Radioanalytical and Nuclear Chemistry, 2021, 328 : 691 - 699
  • [43] A study on the fretting corrosion of 316L in static lead-bismuth eutectic (LBE): The role of slip amplitude and normal force on damage mechanism at 350 °C
    Chen, Hui
    Pei, Wenjie
    Zhang, Shengzan
    Tan, Wei
    Zhu, Guorui
    JOURNAL OF NUCLEAR MATERIALS, 2025, 603
  • [44] Silicon-containing ferritic/martensitic steel after exposure to oxygen-containing flowing lead-bismuth eutectic at 450 and 550 °C
    Schroer, Carsten
    Koch, Verena
    Wedemeyer, Olaf
    Skrypnik, Aleksandr
    Konys, Juergen
    JOURNAL OF NUCLEAR MATERIALS, 2016, 469 : 162 - 176
  • [45] Low cycle fatigue behavior of 316LN stainless steel hollow specimen in air and liquid lead-bismuth eutectic
    Ding, Jianhua
    Tan, Jibo
    Zhang, Ziyu
    Wang, Xiang
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 175
  • [46] The effects of cold working on the corrosion behavior of an austenitic stainless steel in liquid lead-bismuth eutectic under vacuum at 873 K
    Bian, Lu
    Xia, Shuang
    Bai, Qin
    Li, Hui
    Zhou, Bangxin
    JOURNAL OF NUCLEAR MATERIALS, 2018, 509 : 591 - 599
  • [47] TWIN ASTIR: First tensile results of T91 and 316L steel after neutron irradiation in contact with liquid lead-bismuth eutectic
    Van den Bosch, J.
    Coen, G.
    Bosch, R. W.
    Almazouzi, A.
    JOURNAL OF NUCLEAR MATERIALS, 2010, 398 (1-3) : 68 - 72
  • [48] Performance of the new ferritic/martensitic steel SIMP against liquid lead-bismuth eutectic corrosion: Comparison with T91 and 316L steels
    Ma, Zhiwei
    Shen, Tielong
    Zhou, Ting
    Wang, Zhiguang
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2023, 74 (02): : 221 - 232
  • [49] Atomic-scale dissolution corrosion mechanism of additively-manufactured 316L steels in liquid lead-bismuth eutectic
    Gong, Xing
    Wan, Li
    Gao, Mingxin
    Auger, Thierry
    Chen, Kaiyun
    Wang, Pei
    Short, Michael P.
    Liu, Jing
    Luo, Jian
    ACTA MATERIALIA, 2025, 290
  • [50] SMALL PUNCH TESTS ON AUSTENITIC 316L STEEL SAMPLES PRE-EXPOSED IN LIQUID LEAD ENVIRONMENT
    Olaru, Valentin
    Radu, Vasile
    Dupleac, Daniel
    UPB Scientific Bulletin, Series B: Chemistry and Materials Science, 2024, 86 (03): : 307 - 324
12345