The roles of Ni segregation on the oxidation kinetics of austenitic stainless steel 316L exposed to oxygen-containing liquid lead-bismuth eutectic (LBE)

被引：0
|
作者：
Guo, Shaoqiang [1 ]
Chen, Jianye [1 ]
Ma, Zelin [1 ]
Du, Qian [1 ]
Lu, Chenyang [1 ]
Xie, Shijing [1 ]
Long, Bin [2 ]
Yun, Di [1 ]
Gu, Long [3 ]
机构：
[1] Xi An Jiao Tong Univ, Sch Nucl Sci & Technol, Shaanxi Key Lab Adv Nucl Energy & Technol, Xian 710049, Shaanxi, Peoples R China
[2] China Inst Atom Energy, POB 275-92, Beijing 102413, Peoples R China
[3] Lanzhou Univ, Sch Nucl Sci & Technol, Lanzhou 730000, Gansu, Peoples R China
来源：
CORROSION SCIENCE | 2025年 / 244卷
基金：
中国国家自然科学基金;
关键词：
A. Austenitic steel; B; TEM; EBSD; C. Liquid metal corrosion; C; Oxidation; FERRITIC-MARTENSITIC STEELS; LONG-TERM BEHAVIORS; FE-9CR-1MO STEEL; DEGREES-C; ELECTRON-MICROSCOPY; CORROSION BEHAVIOR; OXIDE SCALES; MECHANISM; TEMPERATURE; ALLOY;
D O I：
10.1016/j.corsci.2024.112644
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The micro-to-atomic structure of the oxide scale formed on AISI 316L austenitic stainless steel exposed to oxygen- containing liquid LBE at 550 degrees C is characterized by SEM-EDS, EBSD, FIB-TEM and synchrotron radiation microXRD. Nickel that was believed to be detrimental to steel corrosion in Pb-Bi is revealed to be beneficial on retarding the oxidation kinetics. Ni was not oxidized and existed as metallic Ni-rich nanophase in the internal oxidation zone (IOZ). The inward diffusion of Ni from IOZ to the bulk steel caused the segregation of coarse Nirich precipitates on grain boundaries and the steel/IOZ interface, which hindered the intergranular and possibly the trans-granular diffusion.
引用
收藏
页数：17
相关论文
共 50 条
  • [1] Selective leaching of nickel and chromium from Type 316 austenitic steel in oxygen-containing lead-bismuth eutectic (LBE)
    Schroer, Carsten
    Wedemeyer, Olaf
    Novotny, Josef
    Skrypnik, Aleksandr
    Konys, Juergen
    CORROSION SCIENCE, 2014, 84 : 113 - 124
  • [2] Effect of deformation twinning on the early oxidation behaviour of 316L steel exposed to liquid lead-bismuth eutectic
    Ma, Zhiwei
    Jin, Peng
    Zhou, Ting
    Chang, Hailong
    Gao, Xing
    Shen, Tielong
    Wang, Zhiguang
    VACUUM, 2024, 227
  • [3] Analysis of bi-layer oxide on austenitic stainless steel, 316L, exposed to Lead-Bismuth Eutectic (LBE) by X-ray Photoelectron Spectroscopy (XPS)
    Koury, D.
    Johnson, A. L.
    Ho, T.
    Farley, J. W.
    JOURNAL OF NUCLEAR MATERIALS, 2013, 440 (1-3) : 28 - 33
  • [4] Revealing fretting corrosion synergistic mechanism of 316 stainless steel in liquid lead-bismuth eutectic (LBE)
    Hua, Ke
    Cao, Yue
    Li, Na
    Tong, Yanlin
    Song, Yifan
    Zhang, Fan
    Li, Xiaolin
    Wu, Hongxing
    Wang, Haifeng
    CORROSION SCIENCE, 2023, 215
  • [5] Crevice corrosion behavior of 316L austenitic steel in static liquid lead-bismuth eutectic at 550°C
    Huang, Yuji
    Meng, Fanqiang
    Shi, Jiajian
    Zhang, Lijun
    Yuan, Rui
    Chen, Yingxue
    Zhang, Feifei
    JOURNAL OF NUCLEAR MATERIALS, 2025, 603
  • [6] Spectroscopic and microscopic investigation of the corrosion of 316/316L stainless steel by lead-bismuth eutectic (LBE) at elevated temperatures: importance of surface preparation
    Johnson, AL
    Parsons, D
    Manzerova, J
    Perry, DL
    Koury, D
    Hosterman, B
    Farley, JW
    JOURNAL OF NUCLEAR MATERIALS, 2004, 328 (2-3) : 88 - 96
  • [7] The role of lead-bismuth eutectic temperature in affecting fretting corrosion of 316L stainless steel
    Chen, Hui
    Feng, Zhipeng
    Mei, Guiyu
    Tan, Wei
    Zhu, Guorui
    WEAR, 2025, 572
  • [8] Fatigue crack initiation in lead-bismuth eutectic and its effect on the cyclic stress behaviour of austenitic stainless steel 316L
    Solis, Noelia Olivia Fuentes
    Gavrilov, Serguei
    Seefeldt, Marc
    Wevers, Martine
    JOURNAL OF NUCLEAR MATERIALS, 2024, 600
  • [9] Dissolution corrosion of 316L austenitic stainless steels in contact with static liquid lead-bismuth eutectic (LBE) at 500 οC (vol 490, pg 9, 2017)
    Lambrinou, K.
    Charalampopoulou, E.
    Van der Donck, T.
    Delville, R.
    Schryvers, N.
    JOURNAL OF NUCLEAR MATERIALS, 2017, 490 : 345 - 345
  • [10] Influence of Plastic Deformation on Dissolution Corrosion of Type 316L Austenitic Stainless Steel in Static, Oxygen-Poor Liquid Lead-Bismuth Eutectic at 500°C
    Klok, Oksana
    Lambrinou, Konstantina
    Gavrilov, Serguei
    Stergar, Erich
    Van der Donck, Tom
    Huang, Shuigen
    Tunca, Bensu
    De Graeve, Iris
    CORROSION, 2017, 73 (09) : 1078 - 1090
12345