High temperature oxidation and carburizing mechanisms of Cr35Ni45 heat-resistant steel under service conditions

被引：0

作者：

Song, Ruo-Kang ^{[1
]}

Zhang, Mai-Cang ^{[1
]}

Peng, Yi-Chao ^{[1
]}

Du, Chen-Yang ^{[2
]}

Zheng, Lei ^{[1
]}

Yao, Zhi-Hao ^{[1
]}

Dong, Jian-Xin ^{[1
]}

机构：

[1] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing

[2] China Special Equipment Inspection and Research Institute, Beijing

来源：

Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2014年 / 36卷 / 08期

关键词：

Carburization; Heat-resistant steel; High temperature; Oxidation;

D O I：

10.13374/j.issn1001-053x.2014.08.009

中图分类号：

学科分类号：

摘要：

The oxidation and carburizing mechanisms of Cr35Ni45 type pyrolysis furnace tubes serviced for different time (as-cast, 1.5 a and 6 a) were systematically investigated by scanning electron microscopy (SEM), electron probe and X-ray diffraction (XRD). Compared with original uniform microstructure distribution, there are three zones including an oxidation layer, a carbide depletion zone and a carbide-rich zone at the subsurface region of the Cr35Ni45 tube inner wall after long time service. The oxidation behavior of the Cr35Ni45 tubes at high temperature consists of the external oxidation of chromium and the internal oxidation of silicon, and the outer oxidation layer is greatly affected by repeated destruction and reformation in decoking. The carburizing behavior of the Cr35Ni45 tubes mainly results from coking on the inner wall surface, and repeated destruction of the outer oxidation layer can aggravate this carburization. But due to auto-remediation of the outer oxidation layer, carburization of both the serviced tubes is at a lesser degree. Also, repeated destruction and reformation of the outer oxidation layer cause the depletion of Cr, the increase in critical concentration of C in the subsurface of the inner wall and carbide participation at the below region, leading to the formation of a carbide depletion zone and a carbide-rich zone.

引用

页码：1045 / 1051

页数：6

共 26 条

[1] Kaya A.A., Krauklis P., Young D.J., Microstructure of HK40 alloy after high temperature service in oxidizing/carburizing environment, 49, (2002)
[2] Khodamorad S.H., Rezaie H., Sadeghipour A., Et al., Analysis of ethylene cracking furnace tubes, 21, (2012)
[3] Voicu R., Andrieu E., Poquillon D., Et al., Microstructure evolution of HP40-Nb alloys during aging under air at 1000 ℃, 60, (2009)
[4] Laigo J., Christien F., Le G.R., Et al., SEM, EDS, EPMA-WDS and EBSD characterization of carbides in HP type heat resistant alloys, 59, (2008)
[5] Sustaita-Torres I.A., Haro-Rodriguez S., Guerrero-Mata M.P., Et al., Aging of a cast 35Cr-45Ni heat resistant alloy, 133, (2012)
[6] Shi S., Lippold J.C., Microstructure evolution during service exposure of two cast, heat-resisting stainless steels HP-Nb modified and 20-32Nb, 59, (2008)
[7] Shen L.M., Gong J.M., Tang J.Q., Et al., Study on the carburization resistance of Cr25Ni35Nb and Cr35Ni45Nb alloys for ethylene cracking furnace tube at high temperature, 44, 5, (2010)
[8] Shen L.M., Geng L.Y., Gong J.M., Effects of aging time on mechanical properties and microstructure in Cr35Ni45Nb centrifugally cast austenitic steel, 33, 2, (2011)
[9] Piekarski B., Effect of Nb and Ti additions on microstructure and identification of precipitates in stabilized Ni-Cr cast austenitic steels, 47, (2001)
[10] Wang W.Z., Xuan F.Z., Wang Z.D., Et al., Effect of overheating temperature on the microstructure and creep behavior of HP40Nb alloy, 32, 7, (2011)

← 1 2 3 →