Structure analysis of thin corrosion products film on hot-dip Zn-Al coatings by synchrotron radiation photoemission spectroscopy

被引：0

作者：

Nishihara, Katsuhiro ^{[1
,2
]}

Matsumoto, Masamitsu ^{[1
]}

Kimoto, Masanari ^{[1
]}

Kudo, Takeo ^{[1
,2
]}

Uchida, Hitoshi ^{[2
]}

Haruyama, Yuichi ^{[3
]}

Kanda, Kazuhiro ^{[3
]}

Matsui, Shinji ^{[3
]}

机构：

[1] Corporate Res. and Development Lab., Sumitomo Metal Industries LTD., Amagasaki, 660-0891, 1-8, Fuso-cho

[2] Graduate School of Engineering, University of Hyogo, Himeji, 671-2280

[3] Lab. of Advance Sci. and Tech. for Industry, University of Hyogo, kamigori, Ako, Hyogo, 678-1205, 3-1-2, Koto

来源：

Zairyo to Kankyo/ Corrosion Engineering | 2007年 / 56卷 / 07期

关键词：

Corrosion mechanism; Corrosion products; Film structure; FT-IR; Hot-dip Zn-Al alloy coating; NaCl; Photoemission spectroscopy; SR;

D O I：

10.3323/jcorr.56.314

中图分类号：

学科分类号：

摘要：

Structure of thin corrosion products film (CPF) on hot-dip Zn-Al alloy coated steel sheets were investigated by means of photoemission spectroscopy using synchrotron radiation of 160 eV and μ-FT-IR method, and were compared with those on Zn and Al pure metal sheets. CPF was prepared by 1 h and 16 h exposure in air saturated with water vapor at 323 K under the presence of NaCl particles. As a result, the dominant component of the CPF on the Zn-0.2%Al coating changed from Zn(OH)2 to 2ZnCO3·3Zn(OH) 2, while the CPF of Zn-55%Al alloy coating was consisted mainly of ZnCl2·4Zn(OH)2. And it was found that the structure near the surface of CPF, which was composed mainly of Al oxide, was transformed into the surface structure covered with Al chloride by humid exposure under the presence of NaCl.

引用

页码：314 / 320

页数：6

共 20 条

[1]

Sagiyama M., Research Report for Fundamentals of Corrosion Protection and Evaluation Methods on Zinc and Zinc alloy Coated Steels, (2005)

[2]

Hoboh Y., J. Surf. Finish. Soc. Jpn, 42, (1991)

[3]

Blickwede D.J., Tetsu-to-Hagane, 66, (1980)

[4]

Oka J., Asano H., Takasugi M., Yamamoto K., Tetsu-to-Hagane, 68, (1980)

[5]

Uchiyama Y., Hasaka M., Koga K., Transact. Jpn. Inst. Met, 27, (1986)

[6]

Nishihara K., Kimoto M., Kudo T., Uchida H., Haruyama Y., Kanda K., Matsui S., Proc. Asia Steel Int. Conf, (2006)

[7]

Brundle C.R., J. Vac. Sci Tecnol, 11, (1974)

[8]

Seah M.P., Dench W.A., Surf. Interf. Anal, 1, (1979)

[9]

Tokutaka H., Nishimori K., Hayashi H., Surf. Sci, 149, (1985)

[10]

Keddam M., Hugot-Le-Goff A., Takenouti H., Thierry D., Arevalo M.C., Corros. Sci, 33, (1992)

← 1 2 →