Synthesis of Long Afterglow Phosphors Doped B SrAl2O4:Eu2+, Dy3+ and Its Luminescent Properties

被引：0

作者：

School of Materials and Engineering, Changchun Science and Technology University, Changchun, 130022, China ^{[1
]}

不详 ^{[2
]}

不详 ^{[3
]}

机构：

[1] School of Materials and Engineering, Changchun Science and Technology University, Changchun

[2] School of Applied Chemistry, Shenyang Institute of Chemical Technology, Shenyang

[3] School of Materials and Metallurgy, Northeastern University, Shenyang

来源：

J Rare Earth | 2007年 / SUPPL. 1卷 / 86-89期

关键词：

doped B; long afterglow luminescent material SrAl[!sub]2[!/sub]O[!sub]4[!/sub]: Eu[!sup]2+[!/sup; Dy[!sup]3+[!/sup; luminescent properties; materials synthesis and machining technology; rare earths;

D O I：

10.1016/S1002-0721(07)60530-4

中图分类号：

学科分类号：

摘要：

The long afterglow luminescent material SrAl2O4: Eu2+, Dy3+ was prepared by high temperature solid-state method. Effects of doped B on the luminescent properties of phosphors SrAl2O4: Eu2+, Dy3+ were investigated by means of excitation spectra, emission spectra and X-ray diffraction analysis. As the result, the addition of H3BO3 as flux promotes the growth of crystalline and reduces the synthesizing temperature, but the wavelength of emission peak of photoluminescent material did not change with the variation of H3BO3 content. The effect of Dy3+ concentration on the luminescent properties of material was investigated. It was found that the luminescence of phosphors prepared under the condition of the amount of H3BO3 5% and the mole ratio of Eu/Dy = 1/7(Eu = 0.02 mole) had better luminescent property and longer afterglow time. © 2007 The Chinese Society of Rare Earths.

引用

页码：86 / 89

页数：3

共 11 条

[1]

Tang M., Li C., Gao Z., Et al., The study on long persistence of SrAl2O4: Eu2+ [J], Chin. J. Lumin., 16, 1, (1995)

[2]

Matsuzawa T., Aoki Y., Takeuchi N., Et al., A new long phosphorescent phosphor with high brightness, SrAl2O4: Eu2+, Dy3+ [J], J. Eletrochem. Soc., 143, 8, (1996)

[3]

Wang D., Wang M., Research on the phase composition and microstructure of high-efficient phosphor Sr2Al6O11:Eu2+ [J], J. Mater. Sci. Lett., 18, (1999)

[4]

Chen Y., Qiu G., Sun Y., Et al., Studies on super long afterglow luminescence materials [J], J. Rare Earths, 23, 4, (2002)

[5]

Nakazawa E., Mochida T., Traps in SrA12O4: Eu2+, Dy3+ phosphor with rare-earth ion doping [J], J. Lumin., 72-74, (1997)

[6]

Yamamoto H., Matsuzawa T., Mechanism of long phosphorescence of SrAl2O4: Eu2+, Dy3+ and CaAl2O4: Eu2+, Nd3+ [J], J. Lumin., 72-74, (1997)

[7]

Zhang Y., Yin Y., Effects of B2O3 addition on the luminescent properties of Eu2+, Dy3+-co-acrivated strontium aluminate phospuors [J], J. Synthetic Crystals, 32, 1, (2003)

[8]

Song Q., Huang J., Wu M., Study on synthesis and luminescent properities of europum-activated strontium aluminate [J], J. Luminescence, 12, 2, (1991)

[9]

Li D., Lu S., Zang J., Et al., Size confinement and surface state effect of Eu3+: Y2O3 nanocrystals [J], Lumin., 21, 2, (2000)

[10]

Yuan Z., Chang C., Mao D., The effect of H3BO3 on the Sr4Al14O25: Eu2+, Dy3+ phosphor prepared by chemical precipitation method [J], Journal of Functional Materials, 1, 35, (2004)

← 1 2 →