Preparation and characterization of large porous poly(HEMA-co-EDMA) microspheres with narrow size distribution by modified membrane emulsification method

被引：0
|
作者：
Qu, Huanhuan [1 ,2 ]
Gong, Fangling [1 ]
Ma, Guanghui [1 ]
Su, Zhiguo [1 ]
机构：
[1] National Key Laboratory of Biochemical Engineering, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100080, China
[2] Graduate University, Chinese Academy of Sciences, Beijing 100049, China
来源：
Journal of Applied Polymer Science | 2007年 / 105卷 / 03期
关键词：
Porous poly(2-hydroxyethyl methacrylate-coethylene dimethacrylate) [p(HEMA-co-EDMA)] microspheres have important applications in chromatography. In this study; p(HEMA-co-EDMA) microspheres with controllable size were successfully prepared by modified membrane emulsification technique. The CV value of the obtained microspheres was as low as 14.4%. An oil phase mainly composed of toluene was permeated through a membrane with uniform pores into an aqueous phase to form fairly uniform seed emulsion. The secondary emulsion composed of HEMA and EDMA was prepared by a homogenizer. Then; the two emulsions were mixed together. HEMA and EDMA diffused into the aqueous phase; and then were absorbed by the seed droplets. The swollen droplets were further polymerized to prepare monodisperse porous microspheres. It was found that HEMA/EDMA ratio and toluene/monomer ratio showed a significant influence on swelling degree; diameter; and morphology of the obtained microspheres. The swelling degree of the microspheres increased with the increase of toluene/monomer ratio; whereas the average diameter increased with decrease of the ratio. Microspheres with controllable size (28-73 μm) and porosity were obtained; by varying HEMA/EDMA ratios and toluene/monomer ratios. It can be expected that the p(HEMA-co-EDMA) microspheres with controllable size and porosity will provide many advantages in their applications. © 2007 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：1632 / 1641
相关论文
共 39 条
  • [31] Preparation and characterization of stimuli-responsive hydrophilic polysulfone membrane modified with poly (N-vinylcaprolactam-co-acrylic acid)
    Sinha, M. K.
    Purkait, M. K.
    DESALINATION, 2014, 348 : 16 - 25
  • [32] Synthesis of magnetic iron and iron oxide micrometre-sized composite particles of narrow size distribution by annealing iron salts entrapped within uniform porous poly(divinylbenzene) microspheres
    Amara, Daniel
    Grinblat, Judith
    Margel, Shlomo
    JOURNAL OF MATERIALS CHEMISTRY, 2010, 20 (10) : 1899 - 1906
  • [33] Preparation and Characterization of Poly(L-lactide-co-glycolide-co-ε-caprolactone)/1,4-Butanediamine Modified Maleated Poly(D,L-lactide-co-glycolide) Blend Porous Films
    Wang, Dan
    Fang, Jianjun
    Liu, Wenjuan
    Huang, Tianlong
    Zhao, Yanmin
    Duan, Jianglong
    Xie, Hailin
    Chen, Ping
    Zhou, Ziwei
    Zhou, Zhihua
    JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS, 2020, 60 (01): : 51 - 62
  • [34] Preparation and characterization of melittin-loaded poly (DL-lactic acid) or poly (DL-lactic-co-glycolic acid) microspheres made by the double emulsion method
    Cui, F
    Cun, DM
    Tao, AJ
    Yang, MS
    Shi, K
    Zhao, M
    Guan, Y
    JOURNAL OF CONTROLLED RELEASE, 2005, 107 (02) : 310 - 319
  • [35] Preparation and Characterization of a Novel Poly(vinylidene fluoride-co-hexafluoropropylene)/Poly(ethersulfone) Blend Membrane Fabricated Using an Innovative Method of Mixing Electrospinning and Phase Inversion
    Nady, Norhan
    Salem, Noha
    Kandil, Sherif. H.
    POLYMERS, 2021, 13 (05) : 1 - 23
  • [36] Preparation and characterization of hCG-loaded polylactide or poly( lactide-co-glycolide) microspheres using a modified water-in-oil-in-water (w/o/w) emulsion solvent evaporation technique
    Zhu, KJ
    Jiang, HL
    Du, XY
    Wang, J
    Xu, WX
    Liu, SF
    JOURNAL OF MICROENCAPSULATION, 2001, 18 (02) : 247 - 260
  • [37] Preparation and characterization of La0.6Sr0.4Co0.2Fe0.8O3-δ thin-film membrane on porous support by dip-coating method
    Hashim, Salwa Meredith
    Mohamed, Abdul Rahman
    Bhatia, Subhash
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2011, 59 (03) : 505 - 512
  • [38] Preparation and characterization of La0.6Sr0.4Co0.2Fe0.8O3-δ thin-film membrane on porous support by dip-coating method
    Salwa Meredith Hashim
    Abdul Rahman Mohamed
    Subhash Bhatia
    Journal of Sol-Gel Science and Technology, 2011, 59 : 505 - 512
  • [39] Novel method to prepare charged mosaic membrane by using dipole-like microspheres.: I.: Preparation and characterization of poly(4-vinylpyridine/n-butyl acrylate) seed latex with high solid content by soap-free emulsion polymerization
    Ni, HM
    Ma, GH
    Nagai, M
    Omi, S
    JOURNAL OF APPLIED POLYMER SCIENCE, 2000, 76 (12) : 1731 - 1740
1234