Microstructure and mechanical properties of C-Si-Mn TRIP steel prepared by hot rolling

被引：0
|
作者：
Faculty of Material and Chemical Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China [1 ]
不详 [2 ]
机构：
来源：
Cailiao Kexue yu Gongyi | 2008年 / 3卷 / 319-321期
关键词：
Austenite - Tensile strength - Tensile testing - Hot rolling - Yield stress - High strength steel - Plasticity - Manganese alloys - Silicon alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
To reveal the relationship between the microstructure, mechanics properties and the process, a TRIP steel was prepared by hot rolling and controlling cooling in laboratory. The microstructure of the steel was studied by OP, SEM and TEM. The results of tensile tests indicated that the mechanics properties of experimental TRIP steels were tensile strength of 605 MPa, yield strength of 440 MPa, high elongation of 28.4% and ratio of yield strength to tensile strength of 0.73. The results indicated that the microstructure was composed of ferrite, bainite and retained austenite. The results of quantitative colour metallography showed that retained austenite fraction was around 5.6%.
引用
收藏
相关论文
共 50 条
  • [31] Heat treatment, microstructure and mechanical properties of a C-Mn-Al-P hot dip galvanizing TRIP steel
    Ding, Wei
    Hedstrom, Peter
    Li, Yan
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 674 : 151 - 157
  • [32] Effects of Distributions of Constituent Phases on Mechanical Properties of C-Si-Mn Dual-phase Steel
    Nakagaito, Tatsuya
    Yamashita, Takako
    Yokota, Takeshi
    Terada, Yoshihiro
    Kajihara, Masanori
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2022, 108 (06): : 370 - 382
  • [33] Effect of Thermomechanical Control Processing on Microstructure and Mechanical Properties of Fe-0.2C-1.44Si-1.32Mn Hot Rolled TRIP Steel
    ZHANG Zi-cheng
    Journal of Iron and Steel Research(International), 2010, 17 (07) : 44 - 50
  • [34] Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling
    Jiang, Jun
    Ding, Hua
    Luo, Zong-an
    Xie, Guang-ming
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2018, 25 (07) : 732 - 738
  • [35] Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling
    Jun Jiang
    Hua Ding
    Zong-an Luo
    Guang-ming Xie
    Journal of Iron and Steel Research International, 2018, 25 : 732 - 738
  • [36] Effects of austempering after hot deformation on the mechanical properties of hot rolled Si-Mn TRIP steel sheets
    Li, Z
    Zhang, PL
    Wu, D
    14TH CONGRESS OF INTERNATIONAL FEDERATION FOR HEAT TREATMENT AND SURFACE ENGINEERING, VOLS 1 and 2, PROCEEDINGS, 2004, : 248 - 251
  • [37] Effects of Austempering after Hot Deformation on the Mechanical Properties of Hot Rolled Si-Mn TRIP Steel Sheets
    LI Zhuang1*2
    材料热处理学报, 2004, (05) : 248 - 251
  • [38] Microstructure and Mechanical Properties of a TRIP Steel Containing 7 Mass% Mn
    Park, Seong-Jun
    Oh, Chang-Seok
    Kim, Sung-Joon
    ADVANCED STEELS: THE RECENT SCENARIO IN STEEL SCIENCE AND TECHNOLOGY, 2011, : 275 - 278
  • [39] EFFECT OF CARBON CONTENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF COLD-ROLLED C-Mn-Al-Si TRIP STEEL
    Fu Bo
    Yang Wangyue
    Li Longfei
    Sun Zuqing
    ACTA METALLURGICA SINICA, 2013, 49 (04) : 408 - 414
  • [40] Effect of heat treatment on microstructure and mechanical properties of cold rolled C-Mn-Si TRIP-aided steel
    Srivastava, Ashok Kumar
    Jha, G.
    Gope, N.
    Singh, S. B.
    MATERIALS CHARACTERIZATION, 2006, 57 (02) : 127 - 135
12345